钢铁研究学报(英文版)
Abstract： Microstructure evolution and mechanical properties of newly designed 01C-6Mn-05Si-1Al TRIP-aided steels under different annealing conditions and the effects of matrix microstructure before intercritical annealing on the final microstructure were studied by means of X-ray diffraction (XRD), scanning electron microcopy (SEM), dilatometric simulation, optical microstructure (OM) and tensile testing in this work. The experimental results indicate that the TRIP steel with Mn of 6% could form a considerable amount of retained austenite with good TRIP effect after a simple intercritical annealing treatment, and the matrix microstructure before intercritical annealing treatment can greatly affect the final microstructure. The original microstructure of the ferritic matrix steel was eliminated, while annealed martensite was remained from the martensite matrix steel under the same intercritical annealing conditions.
关键词:
Key words: high manganese TRIP steel
,
intercritical annealing
,
microstructure
,
mechanical properties