Li QU Jing-long
,
BI Zhong-nan
,
DU Jin-hui
,
WANG Min-qing
,
WANG Qing-zeng
,
ZHANG Ji
钢铁研究学报(英文版)
The hot deformation characteristics of GH4720Li alloy were studied at the temperature of 1100-1170 ℃ and strain rate of 001-1 s-1 using Gleeble hot compression tests. True stress-true strain curves and deformation microstructures were investigated. Constitutive equation was established using the hyperbolic law. Processing map for hot working was also developed on the basis of the variations of efficiency of power dissipation with temperature and strain rate. The results show that dynamic recrystallization is the dominant softening mechanism during hot deformation. Fully recrystallized grain is obtained at strain of 07 above 1130 ℃, and coarsening occurs above 1150 ℃. The mean deformation activation energy is determined to be 512 kJ/mol. According to the low activation energy value, high dissipation efficiency parameter and fine recrystallized microstructure, 1130 ℃ is chosen as the hot working temperature for GH4720Li alloy.
关键词:
hot deformation
,
GH4720Li alloy
,
constitutive equation
,
processing map