THE CREEP AND FRACTURE BEHAVIOR OF TWO NICKEL-BASED SUPERALLOYS

S.H.Ai , Y.B.Xia and J.F.Tian (State Key Laboratory for Fatigue and Fracture of Materials , Institute of Metal Research , The Chinese Academy of Sciences , Shenyang 110015 , China)

金属学报(英文版)

The creep and fracture behavior of the cast K417 and forged GH4049 nickel-based superalloys were investigated in the temperature range of 700-900℃ C. Within the ranges of stress and temperature studied, the steady state creep rates exhibited a power law relationship with the applied stress and temperature. The time to rupture is inversely proportional to the steady state creep rate. Under all testing conditions, the creep fracture process was mainly controled by crack initiation and growth of the intergranular oxidation. Casting porosities, pores and carbides were also prefecentral locations of creep crack initiation in the cast K417 alloy. In addition, the intergranular fracture feature in the forged GH4049 alloy was apparently associated with the formation and coalescence of the cavitations on the grain boundaries.

关键词: superalloy , null , null

出版年份

刊物分类

相关作者

相关热词