Lanzhang ZHOU
,
Jianting GUO
材料科学技术（英）
Reaction-milled NiAl-TiB2 composite was fabricated by mechanical alloying elemental powders and hot pressing. TiB2 particles are distributed mostly in grain boundaries of the matrix. The compressive strain to failure of the composite at RT is about twice that of cast NiAl. The compressive yield stress at high temperatures is about 4.5 times higher than that of extruded NiAl, and is also much stronger than XD NiAl-TiB2 composites. Deformation behavior between 1000-1100℃ with different strain rates has been investigated.
关键词:
Lanzhang ZHOU
,
Valentino LUPINC
,
Jianting GUO
材料科学技术（英）
Thermal stabilities of microstructure and mechanical property have been investigated on superalloy U720Li, which is of great interest of application for jet engine and land-based turbine disc. The results showed that, the primary and secondary gamma' particles maintain good thermal stability at 650 and 700℃ with aging time up to 3000 h, while the tertiary gamma' is apparently dependent on aging temperature and time. The tertiary gamma' particles undergo a procedure of coarsening, dissolution and eventually complete disappearance with the increasing of aging time and temperature. They exhibit unusual high sensibility upon aging temperature, which is attributed to the lattice misfit between the gamma' precipitates and the matrix in the alloy. The grain boundary phase M23C6 remains stable without forming of sigma phase even with aging time up to 3000 h at 700℃. Microhardness decreases apparently with increasing aging time and aging temperature. Theoretical analysis based on dislocation mechanism indicates that the change of microhardness should be attributed to the evolution of the tertiary gamma' during aging.
关键词: