Influence of Pr3+ Doping on the Microstructure of ZnO Quantum Dots

LI Hong , XIA Mengling , LUO Kaifei , WANG Paul W

武汉理工大学学报-材料科学版(英文版) doi:10.1007/s11595-015-1092-y

关键词:

NonMetallic Inclusion Distribution in Surface Layer of IF Steel Slabs

ZHANG Qiaoying , WANG Litao , WANG Xinhua , LI Hong , WANG Wanjun

钢铁研究学报(英文版)

Nonmetallic inclusion distribution in the surface layer of IF steel slabs during unsteady casting was investigated using the original position statistic distribution analysis (OPA) method. It was found that most nonmetallic inclusions larger than 10 μm existed in the subsurface layers of 05-35 mm from the slab surfaces and very few large nonmetallic inclusions were found in the inner regions (≥45 mm from slab surfaces). In addition, it was found that at high casting speed level (14 m/min), even a slight change of casting speed could result in a remarkable increase of the nonmetallic inclusions. Thus, at high casting speed, changing the casting speed should be avoided or considerably lower speed changing rate must be used.

关键词: IF steel;transient casting;slab surface layer;nonmetallic inclusion

Waveform digitizing for LaBr3/NaI phoswich detector

SHE Rui , JI Jian-Feng , FENG Hua , LI Hong , HAN Dong

中国物理C doi:10.1088/1674-1137/38/8/086005

关键词: