JIN Man
,
JIANG Zhonghao
,
NAN Shenghui
,
HU Jiandong
,
LIAN jianshe(Jilin University of Technology
,
Changchun
,
China)(Manuscript received 8 February 1995)Correspondent:LI Geping
,
(Institute of Metal Research
,
Chinese Academy of Sciences
,
Shenyang 110015
,
China)
金属学报(英文版)
The low carbon dual phase structure was cold de formed first,then was tempered at 200 to 600℃.The variation in strength and ductility during tempering of the steel was investigated.It was found that a fter the de formed dual phase structure was tempered at 200 to 600℃, with the increase in the tempering temperature the tensile strength decreases rapidly;the lotal elongation remains constant at 200 to 500℃ but began to rise dramatically at a critical temperature between 500 and 600℃.However,when the non-deformed dual phase structure was tempered at the same temperature range,the tensile strength decreases and the total elongation increases continuously with the increase of temperature.It was demonstrated from TEM analysis that precipitating carbides density along the boundaries ofmartensite lath and the recrystallized grains are responsible for the tempering response ofthe de formed dual phase structure.
关键词:
:de formed dual phase structure
,
null
,
null
JIANG Zhonghao
,
GUAN Zhenzhong
,
ZHANG ZuomeiChangchun Institute of Optics and Fine Mechanics
,
Chinese Academy of Sciences
,
Changchun
,
ChinaLIA N JiansheJilin University of Technology
,
Changchun
,
China
金属学报(英文版)
Bused on the deformation model of dual phase steels, an expression for the stress of martensite in dual phase steels is derived, it predictes that the onset of plastic deformation of martensite (transition strain) depends on the strain hardening of ferrite and on the strength of martensile. The relationship between the flow stress and microstructural parameters of a 0.12C-0.9Mn dual phase steel was investigated using the expression for the flow stress of dual phase steel[1] . By calculating the stress ratio and the stress-strain partition coefficient, the loud transition and the stress-strain partition between two phases are studied. It shows that the deformation of dual phase steel lies between the isostress and isostrain states and the stress-strain pratition changes continuously during the deloramtion.
关键词:
dual phase steel
,
null
,
null
,
null