ZHAO Lihua
,
WU Lijun
,
HUANG Qizhong
,
YANG Qiaoqin 1)(Material Research and Test Center
,
Hunan University
,
Changsha
,
China)2)(Powder Metallurgy Research Institute
,
Center-South University of Technology
,
Changsha
,
China)3)(Laboratory of Atomic Imaging of Solids
,
Institute of Metal Research
,
Chinese Academy of Science
,
Shenyang
,
China)Manuscript received 18 April 1995
金属学报(英文版)
C-B4C-SiC composites with silicon additive obtained by the hot press sintering method are studied by means of transmission electron microscopy(TEM).When the specimens are heated to 1800℃,their structure does not change.When the specimens are heated to 2000℃,carbon begins to graphitize. Moreover,two monoclinic phases are observed.One monoclinic phase named as the M phase belongs to C-center monoclinic lattice with a=0.90nm,b=0.59nm,c=0.54nm and β=119.3°.The other monoclinic phase named as the Ml phase also belongs to C-center monoclinic lattice but with a=0.85nm,b=0.49nm,c=0.53nm and β=123.6°.
关键词:
:C-B_4C-SiC composite
,
null
WU Lijun
,
ZHAO Lihua
,
YANG Qiaoqin
,
LI Shaolu
,
LI Xieqian(Materials Research and Test Centre
,
Hunan University
,
Changsha 410082
,
China)(Laboratory of Atomic Imaging of Solids
,
Institute of Metal Research
,
Chinese Academy of Sciences
,
Shenyang 110015
,
China)
金属学报(英文版)
The structure of Al-Mn-Zn-Mg alloy powder annealed at 800℃ has been studied by transmisston electron microscopy(TEM).An approximant phase(named as C-phase) to the decagonal phase was found and its crystal structure was determined It belongs to c-center orthorhombic lattice with a=2.35 nm,b=3.27 nm and c=1.22 nm.We stillfound a hexagonal phase with a=0.7) nm and c=0.79 nm,(named as phase) in the annealed alloy powder.The annealed alloy powder is composed of the C-phase,the phase,the decagonal phase and Al solid solution.
关键词:
:quasicrystal
,