Al/Al2O3 composites of different ratios were hot-press sintered at 575 similar to 640℃ under a pressure of 30 MPa for 2 h in a vacuum furnace. It was found that the relative density of the Al/Al2O3 composites could be increased evidently with the rise of sinter temperature. No reaction occurred between Al and Al2O3 at the sinter temperatures. Under 640℃-30 MPa-2 h experimental condition, Al/Al2O3 system FGM was successfully fabricated, and its density range changed quasi-continuously from 2.887x10(3) kg/m(3) to 3.1909x10(3) kg/m3 within the middle 1.0 mm thickness range.