H.M.Soliman
,
K.E.Mohamed
,
M.E.Abd El-Azim and F.H.Hammad(Metallurgy Dept.
,
Atomic Energy Authority
,
Cairo
,
Egypt)
材料科学技术（英文）
Low and medium carbon steels were aluminized by the pack aluminizing technique using halideactivated pure-Al and Fe-Al packs. The effect of mixture composition, aluminizing temperatureand time and C content of the steel substrate on the structure and thickness of the aluminidelayer, and on the oxidation resistance was investigated. The optimum oxidation resistance canbe achieved with a low carbon steel substrate when the intermetallic phases Fe3Al and FeAlform the surface of the aluminide layer. In this case, the Al concentration at the surface of thealuminide coating is at least ≥15 wt pct. Formation of high Al concentration phases (FeAl3 andFe2Al5) during aluminizing should be avoided as they tend to embrittle the aluminide layer andreduce its oxidation resistance.
关键词:
H.M.Soliman
,
A.F.Waheed
材料科学技术（英文）
Two different spraying powders [81FVNS and 80% (443)+20% (105)] were plasma sprayed on two types of substrates (AISI 316 and Ti) in order to verify the effect of differential thermal expansion coefficient (DTEC) between coating and substrate on the final residual stresses generated in the coating. Modulus of elasticity (E) was evaluated for the substrates and coatings (as a composite beam). Free-standing coatings were used to measure the thermal expansion coefficient, as a function of temperature, of the actual coatings with all defects, impurities and typical lamella structure. The results show that the residual stresses seems to be less dependent on the linear thermal expansion coefficients mismatching between substrate and coating, reflecting the importance of the other sources of stresses. i.e. quenching or deposition stresses induced during spraying. The suitable heat treatment condition of the coated samples may release some or most of the residual stresses. However in some cases the sign of the stress was completely changed as a result of neglecting the quenching stresses.
关键词: