Hydrogen induced cracking(HIC)of 0.3% C,1% Cr,1% Mn,1% Si high strength steel has been studied under simple mode Ⅰ,mode Ⅱ and(Ⅰ+Ⅱ)mixed mode loading conditions.Af- ter being hydrogen-charged in IN H_2SO_4 solution,the material behaved hydrogen embrittlement in all the cases studied.The threshold K_(ⅡH)/K_(ⅡX) of HIC under mode Ⅱ load- ing was 0.27,which was nearly the same as that K(ⅠH)/K_(ⅠX)=0.29 under mode Ⅰ loading. While the thresholds of-HIC under(Ⅰ+Ⅱ)mixed mode loading were 0.36,0.41 and 0.37 cor- responding to the K_Ⅱ/K_Ⅰ ratio of 0.27,0.4 and O.81.The results show that simple mode Ⅰ or mode Ⅱ loading is more susceptible to hydrogen embrittlement than(Ⅰ+Ⅱ)mixed mode. For explaining the experimental results,the effects of triaxial stress as well as plastic deformation ahead of crack tip has been discussed.
关键词:
(Ⅰ+Ⅱ)mixed mode
,
null