Galvanic compatibility between graphite epoxy composite materials (GECM) and LY12CZ aluminum alloy was evaluated in different atmospheric corrosion environ-ments and by laboratory electrochemical measurements.Open circuit potential elec-trochemical measurements showed a relatively large potemtial difference about 1 volt between the GECM and LY12CZ aluminum alloy,and this difference provided the driving force for galvanic corrosion of the LY12CZ aluminum alloy as an anode. Having been exposed for 1,3or 5years in Beijing,Tuandao and Wanning station,GECM/LY12CZ couples showed significant losses of strength and elongation.Protec-tive coatings and non-conductive barriers breaking the galvanic corrosion circuit were evaluated under the same atmospheric corrosive conditions.Epoxy primer paint,glass cloth barriers and LY12CZ anodizing were effective in glvanic corrosion control for GECM/LY12CZ couples.
关键词:
galvanic corrosion
,
null
,
null
F.Lu
,
W.Y.Shen
,
J.G. Li and W.D. Zhen(Beijing Institute of Aeronautical Materials
,
Beijing 100095
,
China Manuscript received 26 August 1996)
金属学报(英文版)
The electrochemical approach was used to show the nature of the galvanic corrosion when graphite epoxy composite materials(GECM)were coupled to LY12CZ aluminum alloy. An open circuit potential difference of one volt was obtained in 3.5% NaCl solution between GECM and LY12CZ. Corrosion current data (zero impedance technique) indicated that there was serious corrosion at GECM/LY12CZ couple.When GECM/LY12CZ couples were exposed to ASTM salt spray and alternate immersion condition, fiber glass cloth and H06-2 epoxy primer paint were effective methods for preventing galvanic corrosion.The slow strain rate test (SSRT) showed that GECM increased the LY12CZ stress corrosion crack growth rate.
关键词:
:galvanic corrosion
,
null