Z.Q. Wang1
,
2)
,
T.C. Ma2)
,
G.W. Liu2)
,
Y.J. Cai2) and B.L. Lu1) 1) College of Chemical Engineering
,
Dalian University of Technology
,
Dalian 116012
,
China
,
2) Department of Material Science and Engineering
,
Dalian Institute of LightIndustry
,
Dalian 116034
,
China
金属学报(英文版)
Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manometer α Al2 O3 synthesisby LCSwas done, α Al2 O3 withtheparticlesize50 ～80 NM wasgot under properconditions.
关键词:
low temperature combustion synthesis
,
null
,
null
,
null
Z.M. Ding1)
,
Y. Lei2) and L.J. Lao1) 1)Department of Materials Engineering
,
Dalian Railway Institute
,
China 2)Department of Materials Science & Engineering
,
Dalian University of Technology
,
China
金属学报(英文版)
Theacicular austeniteformation process duringintercritical annealing atslow heating speedof0 5 ℃/ min isinvestigated using TEMin the sample of 30 CrMnSiA. The resultsshow thatinthe preliminarystage, austenitesnucleateintheform ofshortneedle atshort rod like cementites, which hasthesame orientation and precipitates along the boundary of original martensitelathes. Asthetemperatureincreasingslowly, the austenites grow up and connect witheach other alongtheboundaryoftheoriginallathesso astoform acicular austenite. At last,the fully grown austenite connectsin the direction verticalto the boundary of lathes, leavingthe remnant ferrites appear in the shape of rhombus, the original austenite grainshaperecovers and the feature of thethick lath remains. The superledgeinterface has been found and someaustenitegrowsintoferritein theshapeoflath.
关键词:
austenitictransformation
,
null
,
null