材料科学技术（英文）
Polycrystalline Fe-Mo-Si-B alloys with grains sized from 15 to 200 nm were prepared by means of the crystallization method. A critical phenomenon was observed in the variations of microhardness and electrical resistivity with respect to the annealing temperature. The critical temperature is 893 K which corresponds to the average grain size of 45 nm.
关键词:
amorphous
,
null
,
null
Honggang JIANG+
,
Bingzhe DING
,
Jingtang WANG
,
State Key Lab. for RSA
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
材料科学技术（英文）
In Ni_(68)P_(18)Cr_(14) amorphous alloy, the dominant component elements Ni and P were in lower content in the surface layer, while Cr was enriched. There was a P enrichment region just below the surface oxide layer, which was supposed to enhance the surface segregation of Cr. Nickel was less oxidized than Cr.
关键词:
Ni_(68)P_(18)Cr_(14)amorphous alloy
,
null