Dong LI
,
Zhentao YU
,
Weisheng TANG
,
Ju DENG
材料科学技术（英文）
NIN has developed a new type of Ti alloy. It is suitable for structure pieces applied in high-temperature and high-pressure water/steam conditions. Its nominal composition is Ti-4Al-2V. In this paper, its microstructure, mechanical properties and corrosion resistance were studied in detail.
关键词:
Weilu WU
,
Zhentao YU
,
Ju DENG
材料科学技术（英文）
The relationships among the deformation, texture and properties of TA16 alloy tube were investigated, an optimum processing parameter was obtained. High Q (the ratio of reduction of diameter to reduction of wall thickness) values increase tensile, flaring properties and reduce flattening, high Q values increase tensile strength, flattening, flaring, and decrease tensile elongation. The main circular textures of rolling tubes are basal (0001) and pyramidal {10(1) over bar 5}, {10(1) over bar 4}, {10(1) over bar 3)}etc., and the main axial textures are prism {10(1) over bar 0} and pyramidal {11(2) over bar 0}, {21(3) over bar 1}, {20(2) over bar 1} etc, under different Q and epsilon values. There are greater changes in the grain size under different epsilon values, compared with that under different Q values.
关键词:
Lin YANG
,
Zhentao YU
,
Ju DENG
材料科学技术（英文）
The corrosion behavior of Ti-2A1-2.5Zr alloy with 5 alloy contents and 5 surface states were studied in water steam at 400℃, 10.3 MPa for 72 h. The weight-increments of all samples are under 4 mg/dm2, better than Zr and Zr-alloy. α-Ti is oxidized into anatase-type TiO2 preferentially. The corrosion resistance is improved by adding Al element or pre-oxidizing treatment, the latter is more effective relatively.
关键词: