The fabrication of TiB2 ceramics with high performance at a relatively low temperature requires a second phase to assist the densification and control the microstructure. Moreover the interface characteristics of composites must also be considered. Nickel was chosen as a good metallic-bearing additive in this study. In order to optimize the interface, Mo was added. The results show that Mo can affect the interreaction between TiB2 and Ni, and metallic liquid plays an important role in limiting the TiB2 grain growth in sintering.
关键词:
Daihua HE
,
Zhengyi FU
,
Qingjie ZHANG
材料科学技术（英）
Combustion reaction welding, one promising method to weld ceramics and metals, was used to weld TiB¬2 and Mo. The results showed that the reacted products through combustion reaction were TiB¬2 and MoB when the Mo contents in reactants were 20 wt pct and 40 wt pct while there was Mo besides MoB and TiB¬2 when there were 60 wt pct and 80 wt pct Mo in reactants. Diffusion of elements occurred at the interfaces of the two substrates. The interfaces between the reacted and the two substrates were indistinct after being welded. The welding temperature strongly affected properties of the samples. The value of bending strength of the sample with 80 wt pct Mo in reactant welded at 1500℃ was the highest, 368.52 MPa. The highest value of shear strength among all the samples was that of the one with 40 wt pct Mo in reactant welded at 1500℃, 50.97 MPa.
关键词:
Combustion reaction welding
,
null
,
null
,
null