材料科学技术（英文）
Well-organized mesoporous titania particles and thin films were successfully synthesized by using tetrabutyl titanate as the inorganic precursor and triblock copolymer (Pluronic P123) as the template via evaporationinduced self-assembly process. The resulting materials were characterized by high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD). Fourier-transform infrared spectroscopy (FT-IR), Brunauer-Emmett-Teller (BET) and atomic force microscopy (AFM). Macro shape of mesoporous titania would greatly influence the mesostructure of materials, and the probable reasons were also discussed.
关键词:
mesoporous titania
,
null
,
null
,
null
,
null
,
null
,
null
Shengyu JIANG
,
Jiancheng ZHANG
,
Feng GU
,
Yue SHEN
,
Hua WANG
材料科学技术（英文）
Glass-ceramics containing β-quartz as a main crystal phase based on the system of SiO2-Al2O3-Li2O-K2O-MgO-ZnO were investigated for the application to magnetic storage substrate for higher storage capacity. Parent glasses were prepared, then nucleated and crystallized at certain temperatures for 3~4 h. The crystallization kinetics of glass-ceramics was also studied. The grain size was estimated by Scherrer formula and image treatment of transmission electron microscopy (TEM). The results π showed that the Avrami exponent was determined to be 3.88, the activation energy 189±7 kJ/mol and the grain size 30~60 nm. A detailed microstructure of the glass-ceramics, including grain distribution and the morphology of nano-crystalline was characterized by TEM, X-ray diffraction (XRD), differential scanning calorimeter (DSC), differential thermal analysis (DTA). The relationship between microstructure and mechanical properties was also discussed.
关键词:
Glass-ceramics
,
动力学
,
磁盘基片