W.L.Xu
,
Y.S.Sun
,
S.S.Ding
金属学报(英文版)
Microstructure and tensile properties of Fe3Al-based alloys with additions of TiC andVC particles have been investigated.Results show that the formation of TiC particlesresults in the refinement of the macrostructure of as-cast ingots.Although the additionof VC particles does not cause significant change of the as-cast microstructure,themicrostructure of the alloy after hot-working and recrystallization has been found tobe refined.The formation of both VC and TiC particles results in the increase of yieldstrength,especially at high temperature of 600℃.
关键词:
Fe3Al
,
null
,
null
,
null
,
null
X.G.Min
,
X.Q.Yu
,
Y.S.Sun
金属学报(英文版)
Using the Fe3Al electrode through manual arc surfacing (MAS),Fe3Al coatings havebeen deposited on the stainless steel substrate.The microstructures,hardness andoxidation resistance of the weld overlay have been investigated.The results show thatcrack-free overlays can be obtained when pre-heating of the substrate at 500℃ andpostweld heat treatment at 700℃ were used.Elements of Al,Cr,Ni etc.transferredbetween the substrate and the overlay,but this does not influence the microhardnessof the substrate and the Fe3Al overlay.Oxidation tests show that the Fe3Al overlayshave excellent oxidation resistance in comparison with the stainless steel substrate at800℃ and 900℃.
关键词:
Fe3Al
,
null
,
null