Phase Relations in TiAl+Nb System

Jingguo WANG , Guoliang CHEN , and Zuqing SUN (State Key Lab. for Advanced Metal Materials , University of Science and Technology Beijing , Beijing , 100083 , China)Hengqiang YE (Lab. of Atomic Imaging of Solids , Institute of Metal Research , Academia Sinica , Sh

材料科学技术(英文)

The microstructures and phases of ternary TiAl+Nb alloys containing 50-60 at.-%Al, 0-21 at.-%Nb have been studied using transmission electron microscopy (TEM) and X-ray powder diffraction. The phases present in the alloys and their distribution were found to be a sensitive function of composition. The phase relations between γ-TiAl and γ1 (a new ordered ternary intermetallic compound based on γ-TiAl) were determined. Essentially single γ phase was determined for alloys with relativety low Nb content (≤10 at.-%Nb). the γ1 phase was determined to exist in the composition range containing higher Nb contents (15-21 at.-%Nb). Between γ and γ1 phases, with intermediate Nb contents there is a transitional phase γ1 (a superstructure of γ-TiAl). As for the influence of Al concentration on the phase relations. the γ1 phase was inclined to form in the alloys with relatively high Al contents. The ordering transformation of γ, to γ1 is a continuous ordering process and the transition may be second order.

关键词:

Effect of Spraying Condition and Material Properties on the Residual Stress in Plasma Spraying

Xiancheng ZHANG , Jianming GONG , Sh , ong TU

材料科学技术(英文)

The thermomechanical behavior and the distribution of residual stresses due to thermal spraying of NiCoCrAlY coating were studied by thermomechanical finite element analysis. The effects of phase transformation due to solidifying process of coating particles, thickness and material properties of coating on the residual stresses were discussed. Results showed that residual stress decreases little with the stress relaxation due to the phase transformation. For the substrates with the same thickness, the residual stress increases with the increase in coating thickness. The state of residual stresses relates to the material properties of coating and substrate closely. The stress-induced failure model of coating is also discussed.

关键词: Coating , null , null , null