Y.Z. Lan
,
S. Zhang
金属学报(英文版)
Based on the characteristics of graphite ore from Panzhihua district, the present research tried to find a new technology to increase the purity of the graphite carbon from 93% to 97%. Study was conducted on leaching agents, time, temperature, stirring speed and concentration of leaching solution affecting the process. The technological parameters chosen were: L / S=3:1, reaction time 30min, 5% concentration of sulfuric acid, reaction temperature 70℃, stirring speed 200rev/min. The results of the continuing tests with one kilogram showed that the graphite content can be increased from 93% to 97%, which reaches the requirement for high grade graphite. When waste acid from coke making is used to leach graphite, the result is also satisfactory, but the treatment of waste solution containing organic substances has to be further investigated.
关键词:
graphite ore
,
ore
,
High
,
grade
,
Chemical
,
metho
Y.Z. Lan
,
S. Zhang
金属学报(英文版)
Steel slag is a byproduct produced in large amounts in the steel-making process. It is an important resource that can be effectively utilized. An experiment was described in which steel slag was tested as an adsorbent for the removal of phosphorus from waste water. Phosphorus removal depended on the amount of steel slag added, the pH value, the contact time, and the initial concentration. Under laboratory conditions when the added slag was 7.5g/L, the contact time 2h, and the pH value was equivalent to 6.5, over 99% of the phosphorus was removed; the experimental data on steel slag adsorption of phosphorus in the water fitted the Freundlich isotherm model. Steel slag was found to be very effective in adsorbing phosphorus.
关键词:
steel slag
,
null
,
null