Changsheng XIE
,
Jiansheng ZHAO
,
Peizhen SUN
,
and Xia LIANG (Dept.of Mech. Eng. Ⅱ
,
Huazhong University of Science and Technology
,
Wuhan
,
430074
,
China)(To whom correspondence should be addressed)
材料科学技术(英文)
This paper presents an investigation on the primary microstructure and mechanical properties of a martensite-austenitic duplex steel precipitation-hardened by VC carbide. The results show that the mechanical properties at room temperature are strongly dependent upon the volume fraction of austenite fA. When fA < 32 % both ultimate strength and Vield strength are decreased with increasing fA. however. whenfA>32%, with increasing the.fA. ultimate strength rises and yield strength drops down. Experimental results at elevated temperatures. show that when test temperature ≤500℃. the yield strength to modulus ratio remains unchanged, however. as the temperature rises a substantial fall in the ratio occurs. The strength values at 600 and 700℃ are increased with increasing strain rate measured by cross-head speed of testing rnachine, The law of mixtures and the contribution of strain-induced transformation from unstable austen ite to martensite to the mechanical properties are discussed.
关键词: