The Ni3B phase was formed when boron (0.5 at. pet B) was added to the intermetallic of stoichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni3B phase has the size around 0.1 mu m and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the off-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concentrations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with dislocations up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.