Two methods for predicting residual life of high temperature furnace tubes are studied. One is testanalysis method that is mainly based on the creep rupture tests on postservice specimens. Specimens were taken from the tubes, which had been in service for different times. KachanovRobinsons damage summation concept is employed, however with a modified factor K(ts) to account for prior damage in the specimens. If the foregone total life corresponds with real condition, all of the test data modified by K(ts) should be distributed uniformly nearby the master curve of the new material. The other iscomputer simulation method that considers all of the operating conditions that influence the life. The finite element method (FEM) with iterative calculation is used in the analysis. The variation rates of critical damage element along the wall thickness are determined as a function of the service temperature and current damage. A special program designed based on the method predicts well the residual life of fu
关键词:
residual life
,
null
,
null
,
null
,
null
,
null
Author S.T. TU
,
J.M. Gong and X. Ling Nanjing University of Chemical Technology
,
Nanjing 210009
,
ChinaManuscript received 18 October 1998
金属学报(英文版)
In order to interpret the test results of crossweld specimens for application in practical welded components, the present paper studies the high temperature behavior of laboratory cross weld specimens in terms of the uniaxial material tests and numerical simulations. It is found that the crossweld specimen may be used for the high temperature strength assessment, but can hardly be used for life assessment of the practical welded components, which depends on the loading conditions of the components.
关键词:
high temperature
,
null
,
null
,
null
,
null
J.M. Gong
,
S.T. Tu
,
J. Xia and X. Ling (School of Mechanical Engineering
,
Nanjing University of Chemical Technology
,
Nanjing 210009
,
China)
金属学报(英文版)
Creep deformation localization is generally found in structures at high temperamture,typically in weldments. As the heat affected zone (HAZ) in a weldment is very narrow, deformation in HAZ region can hardly be measured by conventional displacement gauge. A new method for measuring long-term local creep deformation was developed by quartz optical fiber and technique of digital image analysis. The creep deformations of base metal, weld metal and HAZ in weldments are thereby determined with crossweld specimens.
关键词:
creep deformation
,
null
,
null
,
null