This paper describes a way to improve the weld quality through suppressing the porosity formation and restraining the growth of columnar grains by using a weaving beam in laser welding. The experimental results show that the N2 porosity of beam-weaving laser welding low carbon steel can be remarkably reduced with increasing weaving frequency, and porosity can be eliminated when the weaving amplitude is only 0.5 mm; and the Ar porosity in the weld metal is decreased with increasing weaving frequency and amplitude when the welding speed is higher than 0.5 m/min. The beam-weaving laser welding of ultra-fine grained steel has been investigated. The experimental results show that beam-weaving laser welding with appropriate amplitude and frequency can partly restrain the growth of the columnar grain and improve the tensile strength of the weld metal.
关键词:
Welding
,
null
,
null
,
null
Xudong ZHANG
,
Wuzhu CHEN
,
Cheng WANG
,
Lin ZHAO
,
Yun PENG
,
Zhiling TIAN
材料科学技术（英）
3 mm thick 400 MPa grade ultrafine grained ferritic steel plates were bead-on-plate welded by CO¬2 laser with heat input of 120~480 J/mm. The microstructures of the weld metal mainly consist of bainite, which form is lower bainite plates or polygonal ferrite containing quantities of dispersed cementite particles, mixed with a few of low carbon martensite laths or ferrite, depending on the heat input. The hardness and the tensile strength of the weld metal are higher than those of the base metal, and monotonously increase as the heat input decreases. No softened zone exists in heat affected zone (HAZ). Compared with the base metal, although the grains of laser weld are much larger, the toughness of the weld metal is higher within a large range of heat input. Furthermore, as the heat input increases, the toughness of the weld metal rises to a maximum value, at which point the percentage of lower bainite is the highest, and then drops.
关键词:
Laser welding
,
null
,
null
,
null