The microstructural evolution of pearlite during severe cold rolling in Fe-0.8C binary alloy and Fe-1Mn-0.8C ternary alloys was investigated by using SEM, TEM and XRD etc. The results show that the deformed pearlite consists of irregularly bent lamella, coarse lamella with shear-band and fine lamella. As the rolling reduction increases, the proportion of fine lamella increases. The strong plastic deformation, amorphization and dissolution of cementite take place during the severe cold rolling. The maximum carbon content in ferrite reaches 0.15 mass% after 90% cold rolling.
关键词:
Pearlite
,
null
,
null
,
null
,
null
,
null
Ronghua LI
,
Jihua HUANG
,
Sheng YIN
,
Jun ZHAO
材料科学技术（英文）
The hardness variation of two kinds of alloys with 36 wt pct W content and 7/3, 9/1 Ni-to-Fe ratios during strain aging at 800ºC was studied. The microstructures of the aged alloys were analyzed by X-ray diffraction and TEM. The results show that the strain aging hardness of W-Ni-Fe ternary alloy with 7/3 Ni-to-Fe ratio decreases monotonically with the increase of aging time. Under the same conditions, the hardness of 9/1 Ni-to-Fe ratio alloy decreases in the initial aging stage, but then increases as aging process goes on. X ray diffraction and TEM analysis show that there is not any precipitation depositing from the alloy with 7/3 Ni-to-Fe ratio during aging. The monotonic decrease in hardness of this alloy during aging process results from the recovery, recrystallization and solid solubility declining. In the alloy of 9/1 Ni-to-Fe ratio, the fine β phase precipitates dispersively during aging which hardens the alloy. The two different kinds of mechanisms (the softening one and the hardening one) decide the hardness variation of the alloy with 9/1 Ni-to-Fe ratio mentioned above.
关键词:
W-Ni-Fe
,
null
,
null
,
null
,
null