Chungen ZHOU
,
Jingsheng YU
,
Shengkai GONG
,
Huibin XU
材料科学技术（英文）
The oxidation of specimens with thermal barrier coating (TBC) consisted of nickel-base superalloy, low-pressure plasma sprayed Ni-28Cr-6Al-0.4Y (wt pct) bond coating and electron beam physical vapor deposited 7.5 wt pct yttria stabilized zirconia (YSZ) top coating was studied at 1050℃ respectively in flows of O2, and mixture of O2 and 5%H2O under atmospheric pressure. The thermal barrier coating has relatively low oxidation rate at 1050℃ in pure O2. Oxidation rate of thermal barrier coating in the atmosphere of O2 and 5%H2O is increased The oxidation kinetics obeys almost linear law after long exposure time in the presence of 5% water vapor. Oxide formed along the interface between bond coat and top coat after oxidation at 1050℃ in pure O2 consisted of Al2O3, whereas interfacial scales formed after oxidation at 1050℃ in a mixture of O2 and 5%H2O were mainly composed of Ni(Al,Cr)2O4,NiO and Al2O3. It is suggested that the effect of water vapor on the oxidation of the NiCrAlY coating may be attributed to the increase in Ni and Cr ions transport in the oxides.
关键词:
Oxidation
,
null
,
null