PHASE INTERFACE SEGREGATION OF Mg IN A Ni-BASE SUPERALLOY IN100

ZHU Qiang GE Honglin WANG Di CHEN Guoliang University of Science and Technology Beijing , Beijing , China.[Originally published in ACTA METALL SIN(CHINESE EDN)25(3)1989 pp A185—A189 , Dept.of Materials Science and Engineering , University of Science and Technology Beijing , Beijing 100083 , China

金属学报(英文版)

The segregation of Mg to phase interfaces in a nickel base superalloy IN 100 has been investi- gated using EPT(Electron Microprobe Technique).AES(Auger Electron Spectroscopy) and EDS analyses on thin TEM film.The results show that Mg segregates to the phase inter- faces of MC/γ and γ′/γ.The segregation concentration and layer thickness of Mg on MC/γ phase interface are larger than that on γ′/γ phase interface.Mg is not only a grain boundary segregation element,but also a phase interface segregation one.

关键词: magnesium , null , null

University of Science and Technology Beijing

JIA Shizhen University of Science and Technology Beijing , China.

材料科学技术（英）

关键词:

Abstracts of papers from Journal of University of Science and Technology Beijing

稀有金属（英文版）

关键词:

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

Huazhong University of Science and Technology(H.U.S.T)

材料科学技术（英）

关键词:

THE EVOLUTION OF TECHNOLOGY DEVELOPMENT AT GE CORPORATE R & D

T.B.Cox(GE Corporate Research & Development , Niskayuna , NY 12309 , USA Manuscript received 26 August 1996)

金属学报(英文版)

A brief review of the nearly 100 year history of Corporate Researeh and Development at GE is presented. Observations on the changing nature and relevance of industrial research are discussed. Examples of current technology projects for aircraft engine materials are reviewed. Emphasis of these projects is placed on high performance,low cost and high quality.

关键词: :spray forming , null , null