ZHOU Shouzeng ZHANG Jin MA Deqing GAO Maolin University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The magnetic properties,microstructure and magnetic hardening of sintered (Nd_(1-x)Dy_x)_(16)Fe_(77.2)B_(6.8) and Nd_(16)Fe_(77.2)B_(6.8)+ywt-%Dy_2O_3 magnets have been stud- ied.As an addition of Dy to the magnet during smelting,Dy atoms may enter the matrix phase Nd_2Fe_(14)B,so as to enhance H_A,refine grains and improve boundary struc- ture,as well as to increase H_(ci)of the magnet.If Dy_2O_3 is added to powder material prior to sintering,Dy atoms diffuse into the epitaxial layer of grains of matrix phase causing enhancement of K′_1,also refinement of grains and improvement of boundary structure.The NdFeB based permanent magnets with higher H_(ci) and greater(BH)_m may be produced by adding about 2—3 wt-% Dy_2O_3 which make a favourable condition for lower cost.
关键词:
NdFeB magnet
,
null
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null