金属学报(英文版)
A new “mid-relief” plate martensite was observed together with lenticular plate and thin plate martensites in Fe-29.37Ni-0.34C alloy after twice stepped cooling:-100/-120℃, -120/-140℃,-155/-165℃ and -165/-196℃,by means of colour metallography and TEM.The morphology of martensites changes with decreasing M_s temperature.The “mid-relief” plate martensite is characterized by the intensive mid-relie and the substructures of symmetric double twins or half twins and half dislocations,the formation of this martensite can be interpreted by a stress-induced co-generated mechanism.
关键词:
martensite
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
黄爱华
,
金鸣林
,
李和兴
,
房永征
材料导报
试验是以2种含不同QI的煤沥青为原料,采用变径反应管进行热转化反应制备有序性中间相的研究.试验采用偏光显微镜和扫描电镜(SEM)观察了原料各反应阶段的微观结构,考察了QI对热转化过程中中间相有序生长的影响,分析了热转化过程中软化点及族组分的变化.结果表明:少量的喹啉不溶物含量不会阻碍中间相有序的发展.高QI(2.03%)原料易生成镶嵌结构的中间相体,高温处理后样品呈轴状、短纤维、层片松散的石墨化焦结构;含低QI(0.11%)的原料能生成较好的、大区域的中间相体,域结构的中间相体在外力导向和内部裂解气流的作用下容易生成有序的半焦,高温处理后呈大区域、片层紧密、有序性强的细纤维焦结构.同时研究发现,在热转化过程中可通过测定软化点(SP)和TI含量来确定中间相转化程度.软化点约低于250℃、TI为75%左右时为初始中间相区域体形成阶段、半焦生成的前期.
关键词:
煤沥青
,
热转化反应
,
喹啉不溶物
,
中间相
D.Eylon
,
S.R.Seagle
材料科学技术（英文）
The state of Ti research, development and industry is reviewed in this article. The fifty-year anniversary of Ti technology commercialization in the USA provides an opportunity for a historical perspective. Incorporation of "information-age" tools into alloy development, processing, and production invigorates the technology. Consolidation, diversification and globalization have been transforming the Ti industry in the recent years.
关键词:
Yanwu Xu
材料科学技术（英文）
Using mathematical plasticity theories, universal formability (UF) technology has been developed and applied in the automotive stamping engineering and production. As a formability analysis tool, this technology is the major methodology for the development of stamping expert system (solution provider) for (a) product design and feasibility analysis, (b) material automatic selection using nomograms, (c) draw die design using pre-models, and (d) UF and robustness analysis of die performance in finite element analysis (FEA) environment.
关键词:
G.Montay
,
A.Cherouat
,
A.Nussair
,
J.Lu
材料科学技术（英文）
Residual stress in coatings is the result of individual particle stress. Their effects may be either beneficial or detrimental, depending upon the magnitude, sign and distribution of the stresses with respect to the external load. Tensile stress which exceeds the elastic limit causes cracking in surface coatings or at the interface between the substrate and the coat. Compressive stress, in general, has a beneficial effect on the fatigue life, crack propagation, coating adhesion and on the durability of the top coat during service. Compressive residual stresses can increase the number of cycles before crack initiation begins through a mean stress effect. Temperature gradients which occur during solidification and subsequent cooling are the principal mode of internal stresses generation. Some parameters influence the residual stress field of both the coating and the substrate. Substrate nature, spraying temperature, thickness of the coat layer, substrate preparation (grit blasting conditions), and velocity of the splats are in the relation with the quality of the coating. In this work, we will describe the role playing by the ceramics coating elaboration on the residual stress gradient in depth of the component. The incremental hole drilling technique has been developed to determine the residual stress gradient in depth of the coat and substrate which must be used with particularly conditions. This new technology has been employed on zirconia, alumina and tungsten carbide plasma sprayed coating.
关键词:
Coating
,
null
,
null
,
null