钢铁研究学报(英文版)
304 stainless steel coating was deposited on the IF steel substrate by cold gas dynamic spraying (CGDS), and the elastic modulus of the 304 stainless steel coating was studied. The elastic modulus of cold sprayed 304 stainless steel coating was measured using the three-point bend testing and the compound beam theory, and the other mechanic parameters (such as the equivalent flexural rigidity and the moment of inertia of area) of the coatings were also calculated using this compound beam theory. It is found that the calculated results using the above methods are accurate and reliable. The elastic modulus value of the cold sprayed 304 stainless steel coating is 1179×105 MPa, and it is slightly lower than the 304 stainless steel plate (about 2×105 MPa). It indicates that the elastic modulus of the cold sprayed coatings was quite different from the comparable bulk materials. The main reason is that the pores and other defects are existed in the coatings, and the elastic modulus of the coatings also depends on varies parameters such as the feed stock particle size, porosity, and processing parameters.
关键词:
cold gas dynamic spraying
,
304 stainless steel coating
,
three-point bend testing
,
compound beam theory
,
elastic modulus
ZHU Shijie
,
ZHAO Jie
,
WANG Fugang
,
CAO Zhiben Dalian University of Technology
,
Liaoning
,
China. To whom correspondence should be addressed.
材料科学技术（英文）
The effects of the eutectic carbides rand secondary carbides on creep deformation and rupture in smooth bars and CT specimens have been studied. The results show that the resistance of the eutectic carbides of skeleton shape to crack growth is larger than that of the blocky shape carbides. The dendritic segregation of secondary carbides promotes the creep ductility. As the secondary carbide particles become coarser, the creep ductility increases and the crack growth rate decreases. However, if the size of secondary carbide is too large, the creep strength decreases too much and therefore crack growth rate increases.
关键词:
creep
,
null
,
null
,
null
Nuclear Engineering and Design
Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90 degrees, and almost equal to that of the Inconel 600 at impacting angle of 30 degrees. Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600. (C) 2010 Elsevier By. All rights reserved.
关键词:
stress-corrosion cracking;aluminide intermetallic alloys;high-purity;water;mechanical-properties;crevice corrosion;solid particles;wear;behavior;microstructure;deformation;steam
中国腐蚀与防护学报
N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....
关键词:
Europhysics Letters
Noncollinear magnetic investigations of the ground state in PrFeAsO have been performed by the density-functional theory. We calculated the total energy and made structure optimization, and the electronic density of states of PrFeAsO was analyzed. There are three different magnetic structures in PrFeAsO defined by experiments. Based on these magnetic structures, we studied four collinear and four noncollinear cases. The ground state is found to take the ordering proposed by Zhao, in which the FeAs plane is of stripe antiferromagnetism and Pr spins are perpendicular to Fe spins. The electronic density of states indicates that for PrFeAsO the increase of the electron Coulomb interaction leads to a decrease in conductivity. Copyright (C) EPLA, 2011
关键词:
high-temperature superconductivity;phase-diagram;oxypnictides;instability
Nuclear Engineering and Design
A composite coating was deposited on Inconel 600 substrate by cold spray method using pure Ni powder (60 wt.%) blended with alpha-Al(2)O(3) (40 wt.%) as feedstock. It is expected to be applied to repair the bellows eroded by the liquid droplet erosion (LDE). Microstructure of the coating was observed using optical microscope (OM) and scanning electron microscopy (SEM). Microhardness of the coating was determined by Vickers hardness tester. Cavitation erosion (CE) experiments were carried out in the distilled water. Jet impingement erosion (JIE) experiments were performed in slurry containing 1 wt.% quartz particle with the flow velocity of 15 m/s at impingement angles of 30 degrees, 60 degrees and 90 degrees, respectively. Cumulative mass loss vs. testing time was used to evaluate the erosion rate of the coating. The erosion mechanism was analyzed by OM, SEM, X-ray diffraction (XRD) and the microhardness measurement. The results show that the composite coating has compact microstructure and relatively high hardness. The resistance to CE of the coating is not as good as that of Inconel 600 substrate due to the weak bonds of the Al(2)O(3) particles. However, the results of the JIE test indicate that the slurry erosion resistance of the coating is better than that of Inconel 600 at the impact angles of 30 degrees and 60 degrees, but not at the normal impact angle. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
large powder particles;composite coatings;slurry erosion;kinetic;spray;liquid impact;alloy;microstructure;steels;deposition;resistance
刘建国
,
安振涛
,
张倩
,
杜仕国
,
姚凯
,
王金
材料导报
doi:10.11896/j.issn.1005-023X.2017.04.030
为评估氧化剂硝酸羟胺的热稳定性,使用标准液体铝皿于3 K/min、4 K/min、5 K/min加热速率下进行热分析.借助非等温DSC曲线的参数值,应用Kissinger法和Ozawa法求得热分解反应的表观活化能和指前因子,根据Zhang-Hu-Xie-Li公式、Hu-Yang-Liang-Xie公式、Hu-Zhao-Gao公式以及Zhao-Hu-Gao公式,计算硝酸羟胺的自加速分解温度和热爆炸临界温度,并对热分解机理函数进行了研究.设计了7条热分解反应路径,采用密度泛函理论B3LYP/6-311++G(d,p)方法对硝酸羟胺的热分解进行了动力学和热力学计算.计算结果表明,硝酸羟胺热分解的自加速分解温度TsADT=370.05 K,热爆炸临界温度Te0=388.68K,Tbp0=397.54 K,热分解最可几机理函数的微分形式为f(a) =17×(1-α)18/17.硝酸羟胺热分解各路径中,动力学优先支持路径Path 6、Path 5、Path 4和Path 1生成NO和NO2,其次是Path 2、Path 7和Path 3生成N2和N2O.温度在373 K以下时,Path 1'反应无法自发进行,硝酸羟胺无法进行自发的热分解.从热力学的角度来看,硝酸羟胺在370.05K以下储存是安全的.
关键词:
硝酸羟胺
,
热分析
,
热稳定性
,
热分解机理
,
密度泛函理论
涂娜
,
江向平
,
李小红
,
傅小龙
,
杨帆
人工晶体学报
采用传统固相法制备了(1-x)Bi4Ti3 O12-xSrBi2 Nb2 O9(BIT-SBN,x=0,0.025,0.050,0.100,0.150,0.200)铋层状无铅压电陶瓷.系统研究了SrBi2 Nb2 O9掺杂对Bi4Ti3 O12基陶瓷物相结构、微观结构以及jie电性能的影响.结果表明:所有陶瓷样品均为单一的铋层状结构;当SBN掺量为0.100时,样品具有最佳的电性能:d33=21 pC/N,相对密度ρ =98.1％,机电耦合系数kp=8.26％,εr=220,介电损耗tanδ =0.29％,剩余极化强度Pr=9.128 μC/cm2,Tc=594℃.同时,SBN的引入增强了样品的抗老化性和热稳定性.
关键词:
Bi4Ti3O12
,
SrBi2Nb2O9
,
铋层状
,
铁电陶瓷
,
介电性能