STATISTICAL MODEL FOR FRACTURE TOUGHNESS OF A MODIFIED Al-7Si-0.45Mg CAST ALLOY

ZHANG Guobin CHEN Changqi Beijing University of Aeronautics and Astronautics , Beijing , China Dept.of Materials Science and Engineering , Beijing University of Aeronautics and Astronautics , Beijing 100083 , China

金属学报(英文版)

The statistical model for the fracture toughness of a modified Al-7Si-0.45Mg cast alloy has been proposed on the basis of analysis of the correlation between the size distribution of crack nuclei and Si particles and of the micromechanism of fracture.The suitable criterion of frac- ture toughness according to the model has been given.The model has found a good explana- tion for the fracture feature,fracture toughness and microstructure,and agreed with the ex- periments very well.

关键词: cast Al alloy , null , null

University of Science and Technology Beijing

JIA Shizhen University of Science and Technology Beijing , China.

材料科学技术（英文）

关键词:

Abstracts of papers from Journal of University of Science and Technology Beijing

稀有金属（英文版）

关键词:

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

Chen系统的状态变量周期性反馈控制

李开明 , 李亚洲 , 冯维贵 , 林长

量子电子学报 doi:10.3969/j.issn.1007-5461.2007.05.014

采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.

关键词: 混沌 , Chen系统 , 不动点 , Lyapunov指数 , 反馈控制

Ion sputter erosion in metallic glass-A response to "Comment on: Homogeneity of Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass" by L-Y. Chen, Y-W. Zeng, Q-P. Cao, B-J. Park, Y-M. Chen, K. Hono, U. Vainio, Z-L. Zhang, U. Kaiser, X-D. Wang, and J-Z Jiang J. Mater. Res. 24, 3116 (2009)

Journal of Materials Research

The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.

关键词: room-temperature