The microstructural evolution of the gas atomized Fe-25Cr-32C powders was investigated by using optical microscope, scanning electron microscope, and X-ray diffraction. The experimental results showed that the atomized Fe-25Cr-32C powders were mainly composed of austenite and (Fe,Cr)7C3 carbide. Eutectic microstructure was developed in the larger particles, whereas dendritic microstructure was obtained in the particles with diameter less than 38 μm. The reason for microstructure change should be the difference of nucleation undercooling for particles.
关键词:
黄爱华
,
金鸣林
,
李和兴
,
房永征
材料导报
试验是以2种含不同QI的煤沥青为原料,采用变径反应管进行热转化反应制备有序性中间相的研究.试验采用偏光显微镜和扫描电镜(SEM)观察了原料各反应阶段的微观结构,考察了QI对热转化过程中中间相有序生长的影响,分析了热转化过程中软化点及族组分的变化.结果表明:少量的喹啉不溶物含量不会阻碍中间相有序的发展.高QI(2.03%)原料易生成镶嵌结构的中间相体,高温处理后样品呈轴状、短纤维、层片松散的石墨化焦结构;含低QI(0.11%)的原料能生成较好的、大区域的中间相体,域结构的中间相体在外力导向和内部裂解气流的作用下容易生成有序的半焦,高温处理后呈大区域、片层紧密、有序性强的细纤维焦结构.同时研究发现,在热转化过程中可通过测定软化点(SP)和TI含量来确定中间相转化程度.软化点约低于250℃、TI为75%左右时为初始中间相区域体形成阶段、半焦生成的前期.
关键词:
煤沥青
,
热转化反应
,
喹啉不溶物
,
中间相
刘小红
,
王成扬
,
陈明鸣
,
于宝军
材料导报
以软化点相近的高软化点各向同性沥青和各向异性沥青为原料,经溶剂萃取分离出喹啉不溶物(QI),采用偏光显微镜、扫描电镜、元素组成分析、碘吸附测试和X射线衍射分析,对各向异性沥青的光学织构、QI的形貌及其微观结构进行了分析.结果表明,不同原料来源的各向异性沥青会表现出不同的光学各向异性.对高软化点沥青QI的分析表明,虽然母体沥青的软化点相近,但是具有不同光学各向性的沥青分离出的QI在形貌和微观结构上有较大的差异,各向异性沥青QI的分子交联度、芳香度和缩合度均比各向同性沥青QI小,但是平面分子结构更规整,有序度更高.同时发现,当沥青为各向同性时,母体沥青的分子有序度不如QI高,但当沥青为各向异性时,母体沥青的有序度却高于QI.
关键词:
各向同性
,
各向异性
,
高软化点
,
喹啉不溶物
Nuclear Engineering and Design
Liquid droplet erosion (LDE), which often occurs in bellows made of nickel-based alloys, threatens the security operation of the nuclear power plant. As the candidate materials of the bellows, Inconel 600 and Inconel 625 were both tested for resistance to cavitation erosion (CE) and jet impingement erosion (JIE) through vibratory cavitation equipment and a jet apparatus for erosion-corrosion. Cumulative mass loss vs. exposure time was used to evaluate the erosion rate of the two alloys. The surface and cross-sectional morphologies before and after the erosion tests were observed by scanning electron microscopy (SEM), the inclusions were analyzed by an energy dispersive spectroscopy (EDS), and the surface roughness was also measured by surface roughness tester to illustrate the evolution of erosion process. The results show that the cumulative mass loss of CE of Inconel 625 is about 1/6 that of Inconel 600 and the CE incubation period of the Inconel 625 is 4 times as long as that of the Inconel 600. The micro-morphology evolution of CE process illustrates that the twinning and hardness of the Inconel 625 plays a significant role in CE. In addition, the cumulative mass loss of JIE of Inconel 625 is about 2/3 that of Inconel 600 at impacting angle of 90 degrees, and almost equal to that of the Inconel 600 at impacting angle of 30 degrees. Overall, the resistance to CE and JIE of Inconel 625 is much superior to that of Inconel 600. (C) 2010 Elsevier By. All rights reserved.
关键词:
stress-corrosion cracking;aluminide intermetallic alloys;high-purity;water;mechanical-properties;crevice corrosion;solid particles;wear;behavior;microstructure;deformation;steam
许斌
,
李铁虎
复合材料学报
doi:10.3321/j.issn:1000-3851.2003.02.013
根据原生QI杂质由微米级炭粒构成的特性,采用溶剂絮凝法对煤焦油进行了净化处理,以净化煤焦油为原料制备了低QI含量的高性能浸渍剂沥青,对比研究了高性能浸渍剂沥青的流变性能和渗透性能.结果证实:高性能浸渍剂沥青极大地改善了浸渍效果,并且使炭/炭复合材料的力学性能显著提高.
关键词:
炭/炭复合材料
,
浸渍剂沥青
,
原生QI杂质
,
粘度
,
渗透性
,
性能
Nuclear Engineering and Design
A composite coating was deposited on Inconel 600 substrate by cold spray method using pure Ni powder (60 wt.%) blended with alpha-Al(2)O(3) (40 wt.%) as feedstock. It is expected to be applied to repair the bellows eroded by the liquid droplet erosion (LDE). Microstructure of the coating was observed using optical microscope (OM) and scanning electron microscopy (SEM). Microhardness of the coating was determined by Vickers hardness tester. Cavitation erosion (CE) experiments were carried out in the distilled water. Jet impingement erosion (JIE) experiments were performed in slurry containing 1 wt.% quartz particle with the flow velocity of 15 m/s at impingement angles of 30 degrees, 60 degrees and 90 degrees, respectively. Cumulative mass loss vs. testing time was used to evaluate the erosion rate of the coating. The erosion mechanism was analyzed by OM, SEM, X-ray diffraction (XRD) and the microhardness measurement. The results show that the composite coating has compact microstructure and relatively high hardness. The resistance to CE of the coating is not as good as that of Inconel 600 substrate due to the weak bonds of the Al(2)O(3) particles. However, the results of the JIE test indicate that the slurry erosion resistance of the coating is better than that of Inconel 600 at the impact angles of 30 degrees and 60 degrees, but not at the normal impact angle. (C) 2011 Elsevier B.V. All rights reserved.
关键词:
large powder particles;composite coatings;slurry erosion;kinetic;spray;liquid impact;alloy;microstructure;steels;deposition;resistance
唐闲逸
,
魏晓慧
,
许德平
,
张海永
,
贺欣
,
熊楚安
,
唐瀚滢
材料研究学报
doi:10.11901/1005.3093.2015.685
以中温煤沥青为原料,研究其在弹管反应器中的炭化以及“反溶剂法”脱出喹啉不溶物(QI)后的精制沥青的炭化效果.结果表明:含有较高QI的非精制沥青不能制备出较好的针状焦,但在500℃,0.2 MPa,10h的炭化条件下,能够得到相对较优热膨胀系数(CTE)的炭化结果;以煤油和洗油为混合溶剂,反溶剂法能够有效地脱除喹啉不溶物,在芳脂比0.4,沉降温度100℃,搅拌时间0.5 h,沉降时间4h,溶剂比1.8、2的条件下,QI含量分别降到0.0914％和0.0695％,将其在500℃、0.2 MPa、10h的条件下炭化,可制备出热膨胀系数(CTE)较低的针状焦.
关键词:
材料合成与加工工艺
,
中温煤沥青
,
反溶剂法
,
喹啉不溶物
,
炭化
,
针状焦
冀勇斌
,
李铁虎
,
艾艳玲
,
程有亮
,
方长青
功能材料
以煤沥青为原料,采用热聚合的方法,在不同的保温时间下制备出中间相炭微球,通过SEM、激光粒度分析和XRD等分析手段对其表面形貌、粒径分布和微晶结构进行了分析,研究了聚合时间对其球形度、表面QI、粒径分布、微晶结构的影响.结果表明:随着保温时间的延长,中间相炭微球的球形度均较好,表面的QI减少,表面变得比较光滑,粒径分布变得比较集中,微晶结构也较好,当进一步延长保温时间,粒径分布又变得比较分散,微晶结构也变差.
关键词:
中间相炭微球
,
SEM
,
XRD
,
粒径分布