The thin foil specimen of a ferrite-austenite duplex stainless steel was tensiled under transmis- sion electron microscope(TEM).It was found that both in ferrite and austenite the local deformation band at crack tip was formed near to the crack propagating direction.Its forma- tion was related with the crack tip Schmid factor,dislocation shielding,latent hardening and hardening coefficient.When the crack tip emitted dislocations to a slip system by the action of pure mode Ⅱ stress resolute,and the decreasing rate of hardening coefficient was suitable,lo- cal deformation band was easy to form.
关键词:
crack tip
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null