ZHAO Xin
,
YANG Xiao-ling
,
JING Tian-fu
钢铁研究学报(英文版)
In order to investigate the effect of initial microstructure on warm deformation behavior, some specimens of 45 steel were annealed and some quenched. Then the specimens were isothermally compressed on a Gleeble 3500 machine. The deformation temperature range was 550 to 700 ℃ and the strain rate range was 0.001 to 0.1 s-1. An optical microscope (OM) and a transmission electron microscope (TEM) were used to study the microstructures. The results show that the microstructure of annealed specimens is ferrite and pearlite and that of quenched specimens is martensite. The flow stress of quenched specimens is higher than that of annealed ones at 550 ℃ when strain rates are greater than 0.001 s-1. However, at 600 to 700 ℃ and strain rate of 0.001 s-1, the whole flow curves of quenched specimens are below that of annealed ones. Under the rest conditions, the flow stress of quenched specimens is higher at the beginning of compression and then the opposite is true after the strain is greater than a critical value. The microstructure examination proves that the tempering and dynamic recrystallization easily occur in the specimens with martensite during warm compression, which results in the above phenomena.
关键词:
warm deformation
,
flow stress
,
steel
,
microstructure
MAO Weimin University of Science and Technology
,
Beijing
,
100083
,
China.
材料科学技术（英文）
The recrystallization texture in commercially pure Al is investigated after the samples are rolled differently and annealed.The samples with low rol- ling reductions could be generally recovered or recrystallized in situ and characterized by the re- tained G{110}<001>component.This recovery process decreases during annealing with the increase of reduction.The appearance of the B/R{359}. <132>and R{123}<634>components de- pending on the rolling reduction is investigated and the less developed Cube{100}<001>component in commercially pure ahninium is also discussed.
关键词:
recrystallization
,
null
,
null
,
null
Canying CAI
,
Qibin YANG
,
Hongrong LIU
材料科学技术（英文）
Assuming that the wave function , the Schrodinger equation can be written as . Neglecting the last two terms, an analytical expression of electron dynamical diffraction was derived by Qibin YANG et al. In this paper, the analytical expression is modified by further considering the second-order differential term . When the accelerating voltage is not very high, or the sample is not very thin, the reciprocal vector ɡ is large, the modification of the second-order differential is necessary; otherwise it can be neglected.
关键词:
Electron dynamical diffraction
,
null
Ruwei GAO
,
Wei CHEN
,
Jiancheng ZHANG
,
Weicun FONG
,
Wei LI
,
Xiumei LI
材料科学技术（英文）
For both sintered and nanocomposite NdFeB magnets, deltaM(H) of the Henkel plot increases from zero, and reaches a peak, then decreases and changes to the negative values with increasing applied field. This shows that the intergrain interaction changes from the exchange-coup ling type into the magnetostatic interaction type. The magnetic field corresponding to the peak of deltaM(H) is slightly smaller than the coercivity of magnet. The peak of deltaM(H) for aligned sintered magnet is greater than that for misaligned magnet. deltaM(H) peak of the nanocomposite NdFeB magnets increases with decreasing grain sizes. It indicates that the effect of alignment field on the properties of magnet is similar to that of exchange-coupling interaction.
关键词:
TAO Zengyi LUO Jiaming Huazhong University of Science and Technology
,
Wuhan
,
China TAO Zengyi
,
Faculty of Metallic Materials
,
Dept.of Mechanical Engineering No.2
,
Huazhong University of Science and Technology
,
Wuhan 430074
,
China
金属学报(英文版)
The influence of laser surface melting and induction hardening on the surface structure,con- tact fatigue life and failure behaviour of the nodular cast iron has been investigated.The con- tact fatigue life can be improved by both laser treatment and induction hardening,but the fail- ure process and type are different from each other.The former is due to lumpy and deep spal- ling caused by crack propagation between the quenching zone and the substrate,and the latter is due to nubby and surface flaking caused by the oil wedged action into surface cracks.
关键词:
surface hardening
,
null
,
null
,
null
中国腐蚀与防护学报
N。1Atmospheric Corrosivlty for Steels………………………………………………… .LIANG Caideng HO[I i。-tat（6）Caustic Stress Corrosion Cr。king of Alloy 800 Part 2.The Effect of Thiosul执e……………………………………… KONG De-sheng YANG Wu ZHAO Guo-zheng HUANG De.ltL。ZHANG Yu。。he CHEN She。g-bac（13）SERS slid E16CttOCh6iniC81 Stlldy Of Illhibit1Oli M6ch＆tllsth Of ThlollY68 Oil ITOll ID H....
关键词:
刘云川
,
李志华
,
李爱明
材料导报
在EB-PVD/(NiPt)Al涂层中存在皱曲(Rumpling)现象 ,导致涂层的早期失效.综述了皱曲(Rump-ling)力学模型的研究进展,主要包括3个方面的问题:皱曲的力学模型、数值计算方法研究现状;皱曲的机理及力学模型研究中存在的问题和不足;进一步研究皱曲机理并改进模型的途径.提出了在粘结层晶体尺度内棘轮效应与热扩散间存在耦合作用的设想,并认为这种耦合作用是形成皱曲的根本原因.
关键词:
热障涂层
,
皱曲
,
力学模型
,
棘轮效应
,
循环塑性
LIU Shan LU Deyang HUANG Tao ZHOU Yaohe National Lab of Solidification Processing
,
Northwestern Polytechnical University
,
Xi'an
,
China LIU Shan
,
lecturer
,
National Laboratory of Solidification Processing
,
Northwestern Polytechnical University
,
Xi'an 710072
,
China
金属学报(英文版)
An experimental apparatus,which has a convection generator and an aid-heater,is developed for the study of the effect of stable laminar liquid flow on the directional solidification process by the use of transparent alloy SCN-2wt-% Ace.The flow is perpendicular to primary arms. By in-situ observation and photographing at different specific moments,it has been found that such a flow can cause a great change in primary spacings of constrained columnar crystals:for cells,the spacings become smaller;but for dendrites,they become larger.The former is mainly due to the tilted growth of upstreamside branches,while the latter is mainly due to the coup- ling effect of liquid flow with solutal field around dendrite tips.The faster the liquid flows,the further smaller the cell spacing and the further larger the dendrite spacing.
关键词:
forced liquid flow
,
null
,
null
,
null