YANG Wenying LU Fanxiu ZHANG Shouhua University of Science and Technology Beijing
,
Beijing
,
China Department of Materials Science and Engineering
,
University of Science and Technology Beijing
,
Beijing
,
100083
,
China
金属学报(英文版)
The “order-disorder” model was adopted to calculate the lattice vacancies related to the com- position change in Ni_3Al alloys.A great deal of vacancies,i.e.,the non-stoichiometric vacan- cies,may exist in the Ni_3Al alloys containing Al over stoichiometry,i.e.25 at.-%.This was confirmed by the positron annihilation technique.Therefore,the influence of Al content on the enhancing behaviour of B towards the ductility of Ni_3Al alloys can be understood by the interaction of non-stoiehiometric vacancies and B atoms.
关键词:
Intermetallic compounds
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null