Y.Z. Lan
,
S. Zhang
金属学报(英文版)
Based on the characteristics of graphite ore from Panzhihua district, the present research tried to find a new technology to increase the purity of the graphite carbon from 93% to 97%. Study was conducted on leaching agents, time, temperature, stirring speed and concentration of leaching solution affecting the process. The technological parameters chosen were: L / S=3:1, reaction time 30min, 5% concentration of sulfuric acid, reaction temperature 70℃, stirring speed 200rev/min. The results of the continuing tests with one kilogram showed that the graphite content can be increased from 93% to 97%, which reaches the requirement for high grade graphite. When waste acid from coke making is used to leach graphite, the result is also satisfactory, but the treatment of waste solution containing organic substances has to be further investigated.
关键词:
graphite ore
,
ore
,
High
,
grade
,
Chemical
,
metho
Y.Z. Lan
,
S. Zhang
金属学报(英文版)
Steel slag is a byproduct produced in large amounts in the steel-making process. It is an important resource that can be effectively utilized. An experiment was described in which steel slag was tested as an adsorbent for the removal of phosphorus from waste water. Phosphorus removal depended on the amount of steel slag added, the pH value, the contact time, and the initial concentration. Under laboratory conditions when the added slag was 7.5g/L, the contact time 2h, and the pH value was equivalent to 6.5, over 99% of the phosphorus was removed; the experimental data on steel slag adsorption of phosphorus in the water fitted the Freundlich isotherm model. Steel slag was found to be very effective in adsorbing phosphorus.
关键词:
steel slag
,
null
,
null
何恩全
,
马文会
,
刘荣辉
,
于洁
,
戴永年
稀有金属
doi:10.3969/j.issn.0258-7076.2007.04.019
采用了甘氨酸-硝酸盐法制备了La0.7Sr0.3Cr0.5-yMn0.5-zCo(y+z)O3(y, z=0.1, 0.2)系列阳极材料.借助XRD, SEM对所制备的材料进行了物相和形貌分析.XRD表明利用GNP法制得的粉体在1350 ℃烧结5 h可以形成完整的钙钛矿相;SEM分析可知所得物料颗粒呈球状,尺寸约为1 μm,且没有团聚现象.同时,XRD显示La0.7Sr0.3Cr0.5Mn0.4Co0.1O3和La0.9Sr0.1Ga0.8Mg0.2O3电解质之间具有较好的化学相容性.采用直流四探针法测试了不同组成材料在250～800 ℃温度范围内在空气中的电导率,发现该系列材料在该温度段范围符合小极化子导电机制.另外,利用直流四探针法测试了La0.7Sr0.3Cr0.5Mn0.4Co0.1O3在不同还原气氛下的电导率,在CH4和H2气氛中,La0.7Sr0.3Cr0.5Mn0.4Co0.1O3最大电导率分别达到了4.5和0.42 S·cm-1.
关键词:
钙钛矿
,
阳极
,
电导率
黄曼青
,
周全
,
刘峰
,
黄金角
材料导报
doi:10.11896/j.issn.1005-023X.2016.22.010
研究了0~1.4 T的直流磁场对陶瓷型铸造 Mg-Y-Cu-Zr 合金结晶取向和力学性能的影响。结果表明直流磁场对合金的初生相没有明显影响，但磁场强度大于1.12 T时，合金第二相的分布变得不连续。当磁场强度小于0.84 T时，α-Mg在(002)面的衍射峰逐渐增强，但变化不明显；当磁场强度大于0.84 T 时，α-Mg 基体在(002)、(101)面的衍射峰强度明显减弱，而在(100)晶面衍射峰强度有所增强。磁场处理后，合金的综合力学性能得到了改善；当磁场强度为1.4 T 时，其抗拉强度和伸长率最高，分别为237 MPa 和8.5%，较无磁场处理时分别提高了38.6%和33.4%。
关键词:
直流磁场
,
Mg-Y-Cu-Zr合金
,
结晶取向
,
力学性能
Ying Liy Changzhen Wang Zhongli Zhang Jiangxin Wang
材料科学技术（英文）
The steel contains a small amount of hydrogen which will escape during the heat treatment. The hydrogen pressure in 16MnRE steel was investigated with a hydrogen sensor, which used SrCe0:95Yb0:05O3-α proton conductor as a solid electrolyte, YHx+YH2-z as a solid state reference electrode and Ni wire as electrode constructing a hydrogen concentration cell, shown as Ni|YHx+YH2-z |SrCe0:95Yb0:05O3-α |[H]steel |Ni. The response time of sensor is less than 10 s. The relational expression of hydrogen partial pressure with temperatures was determined using two shape proton conductors. The results showed the regularity in experimental temperature range, and the hydrogen partial pressure increased as its temperature was raised.
关键词:
Hydrogen sensor
,
Proton conductor
,
Solid electrolyte
王晓旭
,
陈利
材料工程
doi:10.3969/j.issn.1001-4381.2011.11.001
通过单根Z-pin从复合材料层合板中拔出的试验方法,测试了Z-pin的拔出强度,计算了Z-pin的临界埋入深度,并引入抗拉强度利用率概念来表征Z-pin的抗拉强度在拔出过程中的利用程度.结果表明,直径0.50mm和0.28mm的Z-pin临界埋入深度分别约为5.1mm和3.1mm.当Z-pin的埋入深度小于临界埋入深度时,Z-pin从层板中拔出；Z-pin拔出强度与埋入深度成正比,与Z-pin的直径成反比；当Z-pin的埋入深度大于临界埋入深度时,Z-pin发生断裂,Z-pin的抗拉强度利用率达到100％.最后提出了提高抗拉强度利用率的建议.
关键词:
Z-pin
,
拔出强度
,
复合材料
,
拔出试验
,
抗拉强度