Y.W.Yan1)
,
B.K.Wei2)
,
Z.Y.Fu1)
,
H.T.Lin2) and R.Z.Yuan1) 1) State Key Lab .of Advanced Technologyfor Materials Synthesisand Processing
,
Wuhan University of Technol ogy
,
Wuhan 430070
,
China 2) Institute of Materials
,
Huazhong University of Science and Technology
,
Wuhan 430074
,
China
金属学报(英文版)
Under aircondition,theinsitu TiCP/ Fecompositeshavebeen fabricated by a reactivecast ing route usingtheinexpensiveraw materials. The microstructuresofthecompositehavebeen studied by X ray diffraction,image analyzer and analyticalelectron microscopy. The me chanicalpropertiesand abrasive wearresistanceofboththeas castcompositeandthequenched composite havebeen measured. Theresultsshow thattheinsitu TiCparticles with a average sizeof 4 51μm exhibit a homogenous distribution inthe matrix, and an excellentinterface bonding between the particle and the matrix is achieved. As above microstructure features, thecomposite,especiallythequenched composite, hashigher mechanicalpropertiesand betterwear resistance,compared with high Cr whitecastiron.
关键词:
TiCP/ Fecomposite
,
null
,
null
,
null
,
null
姜迪友
,
刘三秋
稀有金属材料与工程
采用基于密度泛函理论的第一性原理方法研究了钇的含量对W-Y二元合金力学性质的影响,精确计算了W1-xYx(x=0.0625,0.125,0.25,0.5)合金的力学常数,并对其力学特性进行分析.结果表明,W-Y合金的弹性常数、体模量、杨氏模量以及剪切模量随Y含量(原子分数)的增加而成非单调性减小,表明Y对W材料的合金化降低了材料的机械强度.然而,基于力学特性B/G、泊松比v和柯西压力C等分析,Y的合金化对W的延展性和韧性有明显的提高.当Y含量x为0.25时,可有效改善W-Y合金的延展性和抗变形能力.通过态密度分析,W-Y合金的金属性随Y含量的增加先减弱而后增强.
关键词:
第一壁材料
,
W-Y合金
,
力学性质
,
第一性原理
,
密度泛函理论
彭石高
,
丁飞
,
中国有色金属学报
采用溶胶-喷雾干燥-氢还原法制备稀土Y含量分别为0,0.4%,5%,10%和20%的超细(W,Ni,Fe,Y)复合粉末,采用XRD研究煅烧温度和还原温度以及稀土Y含量变化时复合粉末体在制备过程中的相结构变化规律.结果表明:喷雾干燥前驱体随煅烧温度的升高渐渐从非晶体向复合氧化物晶化转变,添加稀土Y的粉末前驱体经煅烧后,Y与W形成复合氧化物Y2W3O12,且稀土Y可以有效地抑制粉末颗粒长大;随着Y含量的增加,Y和W的复合氧化物明显增加,Y2W3O12在700℃才能被还原成低氧复合氧化物相:含5%稀土Y粉末中的Y2W3O12被还原生成新相Y2WO6;当稀土Y增加到10%以上时,不仅生成Y2WO6,还生成另一种新相Y6W2OB15.
关键词:
W-Ni-Fe复合粉末
,
纳米粉末
,
稀土
,
Y
林小辉
,
李来平
,
梁静
,
郑欣
,
喻吉良
复合材料学报
doi:10.13801/j.cnki.fhclxb.20150520.001
为研究Ni基Y2W3O12复合材料的热学性能,首先,采用二次焙烧法制备了负膨胀材料Y2W3O12;然后,将Y2W3O12与金属Ni进行混合,并在1 200℃、50 MPa的条件下热压烧结制得40vol％Y2W3O12/Ni复合材料;最后,对复合材料的成分及热膨胀性能进行了研究.结果表明:在热压烧结过程中,由于Ni的还原性比W差,相对于对比试样40vol％ Y2W3O12/Cr复合材料中发生的复杂化学反应,40vol％Y2W3O12/Ni复合材料的两相之间并未发生反应,使40vol％ Y2W3O12/Ni复合材料保持了较低的热膨胀系数;经数次循环退火释放热应力及去除Y2W3O12相的结晶水后,40vol％ Y2W3O12/Ni复合材料在170～800℃温度范围内的热膨胀系数趋于稳定,约为3.4×10-6 K-1,与理论设计值4.0×10-6 K-1相近.
关键词:
复合材料
,
Y2W3O12
,
负膨胀
,
微观组织
,
热膨胀系数
高原
,
张维
,
王成磊
,
李冰
,
陈选楠
,
黄学锋
,
袁琳
材料热处理学报
研究Q235钢表面等离子W-Mo-Y共渗层的组织、成分、结构、显微硬度,计算渗层中不同位置、浓度下的W、Mo原子扩散系数。结果表明：渗层组织为柱状晶,W、Mo元素呈梯度分布,Y的分布不均匀。共渗层主要结构相为钨钼在α-Fe中的固溶体和Fe17Y2,共渗层显微硬度最高256 HV0.05;Y元素降低表面W、Mo的活度,W、Mo合金元素的化学势变小,表面与基体之间的化学梯度减小,W、Mo原子扩散速率减慢;W-Mo-Y共渗层厚度要比W-Mo共渗层厚度薄;通过Fick第二扩散定律计算表明,在W-Mo-Y共渗和W-Mo共渗时,不同渗层中的W、Mo扩散系数有所不同,但属同一数量级即：10-13～10-14之间。
关键词:
等离子渗金属
,
晶界
,
活度
,
化学梯度
,
化学势
,
Fick第二扩散定律
Journal of Alloys and Compounds
This work mainly investigated the mechanical properties of as-cast Mg-Zn-Y-Zr Mg alloys with Zn/Y ratio about 0.97. Tensile results show that when Zn/Y ratio is constant, the alloy (with Zn and Y contents of 3.93 and 4.14 wt.%, respectively) has the highest strength. XRD analysis shows that the alloys are mainly composed of alpha-Mg matrix and W-phase. With the contents of Zn and Y increasing, the diffraction peaks of W-phase are gradually intensified. In addition, microstructure observation indicates that with the increase of Zn and Y contents, the grain boundaries are gradually coarsened by W-phase. Based on the microstructure observation and fracture analysis, the change of the mechanical properties has been explained. (C) 2007 Elsevier B.V. All rights reserved.
关键词:
Mg-Zn-Y-Zr alloys;the mechanical properties;W-phase;icosahedral phase;microstructure;behavior
李冰
,
高原
,
陈选楠
,
黄学锋
,
赖涛
,
陈文琦
表面技术
doi:10.3969/j.issn.1001-3660.2011.01.025
采用辉光等离子渗金属技术对Q235钢进行W-Mo-Y三元共渗,探讨了极间距、气压、保温时间、温度对共渗层厚度的影响,并分析了共渗层的金相显微组织、合金元素分布及物相组成.结果表明:在试验涉及的条件下,以极间距25 mm,气压30 Pa,保温时间3 h,温度1000℃为最佳工艺参数;共渗层主要由Fe3Mo,Fe(Mo,W,Y),Fe17Y2等组成,组织为柱状晶,W和Mo的含量由表及里逐渐减少,而Y元素由于在晶界处发生偏聚而分布不均匀.
关键词:
等离子渗金属
,
W-Mo-Y共渗
,
Q235钢
王诗阳
,
陈磊
,
沈海丰
,
王玉金
,
傅宇东
材料热处理学报
采用粉末层铺法和无压烧结工艺制备了组元分布指数p分别为0.1、0.3、0.7和1的4种Y2O3-W梯度材料,并进行了4种材料在600℃和400℃温差下的急冷淬火循环热震试验.结果表明:在600℃温差下,经2次循环热震后,4种材料均失效.在400℃温差下,经40次循环热震后,4种材料均未发生失效断裂.随着循环热震次数的增多,热裂纹的长度和密度也随之增加.Y2O3-W梯度材料的抗热震性能随着组元分布指数p的增大逐渐增强.当组元分布指数p=1时,Y2O3-W梯度材料具有最好的抗热震性能.
关键词:
功能梯度材料
,
氧化钇
,
钨
,
循环热震
,
热裂纹
马运柱
,
黄伯云
,
范景莲
,
熊翔
,
魏定池
,
汪登龙
中国稀土学报
以喷雾干燥法制备的(W,Ni,Fe)复合氧化物粉末为原料,采用700 ℃,保温90 min的条件进行还原,研究了La-Y含量对还原制备纳米级W-Ni-Fe复合粉末特性的影响;采用XRD及高倍SEM分别对所制备的复合粉末进行了物相分析、晶粒尺寸测试和形貌观察;并对所制得复合粉末的Fsss粒度、比表面进行了测定与分析.研究结果表明: 不加La-Y时还原粉末由W和γ-(Ni,Fe)两相组成,添加一定量La-Y的还原粉末有W,γ-(Ni,Fe),Y(Ni0.75W0.25)O3和La (Ni0.75W0.25)O3四相组成;当La-Y的质量分数在0～0.8%范围时(占90W-7Ni-3Fe复合粉末的质量分数),随着La-Y含量的增加,粉末dBET粒度由96.6降到50.3 nm,粉末Fsss粒度由0.64降到0.33 μm,粉末晶粒尺寸由26.1降到22.2 nm;未添加La-Y时粉末颗粒为球形,添加一定量的La-Y,粉末颗粒变为近球形或多面体;添加一定量的La-Y不仅可以有效地抑制晶粒长大,还可以在一定程度上提高粉末的分散性.
关键词:
材料学
,
W-Ni-Fe复合粉末
,
纳米级粉末
,
氢还原
,
稀土
闫蕴琪
,
王文生
,
张振祺
,
罗国珍
,
周廉
材料科学与工艺
doi:10.3969/j.issn.1005-0299.2002.02.002
研究了Ti-45Al-8.5Nb-W-Mo-Y合金的相结构.该合金铸态组织大部分由α2+γ片层域团组成,同时含有少量的B2+ω相.经过1200℃,2 h处理后,B2相全部转变成ω相.合金经过70%～80%热变形后,组织由等轴γ晶粒,残余高温B2+ω相,少量的变形片层域团α 2+γ片层组成.变形组织再经过1 280℃,2 h的热处理,其中高温相大幅度减少,同时α2板条增加.挤压态组织由弯曲的片层及少量的等轴γ晶粒组成.循环热处理技术细化组织.
关键词:
TiAl基合金
,
相结构
,
组织转变