WANG Kai
,
XU Tingdong
,
SHAO Chong
,
YANG Chun
钢铁研究学报(英文版)
The data obtained by bending tests for intergranular embrittlement after 45 h and 450 h exposure to Strauss solution have been reported for 304 stainless steel. The results show that an embrittlement peak appears at 650 ℃ for all samples quenched from 1260 ℃ and then sensitized for 150 h at 480, 565, 650, 730, 815 and 900 ℃ respectively. The temperature corresponding to the embrittlement peak is decreased to 565 ℃ when the sensitizing time is prolonged to 1500 h. In this paper, these data are analyzed with an isothermal kinetic model of nonequilibrium grain boundary segregation, indicating that the embrittlement peak is related to the critical time for nonequilibrium grain boundary segregation of sulfur.
关键词:
stainless steel
,
intergranular corrosion
,
nonequilibrium segregation
,
grain boundary
,
sulfur
WANG Kai
,
SI Hong
,
YANG Chun
,
XU Tingdong
钢铁研究学报(英文版)
In virtue of Auger electron spectroscopy, the grain-boundary concentrations of phosphorus in Ni-Cr-Fe superalloy after solution-treated at 1180℃ for 45 min are measured, the results show that a peak of phosphorus concentration occurs at about 180 min during isothermal ageing at 500℃, and a maximum concentration of phosphorus appears also at about 500℃ for all specimens aged for 20 min at temperatures of 200,400,500,700 and 800℃. The results are analysed with the laws of non-equilibrium grain-boundary segregation. It is found from the analysis that peaks are relative to critical time for non-equilibrium grain-boundary segregation of phosphorus.
关键词:
Non-equilibrium segregation;Grain boundaries;Phosphorus;Nickel based superalloys
LIN Jialiu ZHU Shigen YU Zhenzong Tsinghua University
,
Beijing
,
China
金属学报(英文版)
The stress-strain relation for cast low alloy carbon steel at solidification temperature has been examined by the authors' own desingned apparatus for rheological properties measurement.The rheology model,the stress-strain constitutive equation and the rheological parameters therefrom of the cast steel were proposed.Thus the theoretical basis and calcula- ting data for computerized s#nulation on the stress-strain relation and thermal cracking of the cast steel were suggested.
关键词:
rheological behaviour
,
null
,
null
,
null
,
null
Physical Review B
In a recent publication [S. Dong et al., Phys. Rev. Lett. 103, 127201 (2009)], two (related) mechanisms were proposed to understand the intrinsic exchange bias present in oxides heterostructures involving G-type antiferromagnetic perovskites. The first mechanism is driven by the Dzyaloshinskii-Moriya interaction, which is a spin-orbit coupling effect. The second is induced by the ferroelectric polarization, and it is only active in heterostructures involving multiferroics. Using the SrRuO(3)/SrMnO(3) superlattice as a model system, density-functional calculations are here performed to verify the two proposals. This proof-of-principle calculation provides convincing evidence that qualitatively supports both proposals.
关键词:
thin-films;weak ferromagnetism;superlattices;anisotropy;bifeo3;srruo3;model
F.T.Cheng
材料科学技术（英文）
The present communication addresses an interesting problem related to the indeterminacy in hardness of superelastic NiTi reported by Xu et al. The origin of the indeterminacy is attributed to the inadequacy of the conventional Vickers hardness testing measurement which does not record elastic deformation, and thus the indeterminacy may be removed with suitable techniques. Concepts of hardness in relation to deformation are clarified. Recommendations for measuring the hardness of NiTi and other elastic-plastic materials are suggested, together with comments on the advantages and disadvantages of each of these methods.
关键词:
Hardness
,
null
,
null
,
null
,
null
,
null
JIANG Laizhu CUI Kun Huazhong University of Science and Technology
,
Wuhan
,
China
金属学报(英文版)
Studies were made of the calculation of fractal dimension of transverse impact fracture sur- face,and of the correlation between impact toughness of steel and parameters of free-cutting phase by means of the developed fractal geometry model of crack propagation.It is believed that the area fraction,f,of free-cutting phase is negligibly influential to the longitudinal im- pact toughness,as f1 .While the aspect ratio,saying ratio of length to width,of free-cut. ting phase is inversely influential to the transverse impact toughness.This may .be the reason why the transverse impact toughness of free-cutting steel containing more rare earth contrast to sulphur is even higher than the low sulphur containing steel.
关键词:
fractal geometry
,
null
,
null
Liu Zhengyi Fu Jian Zhuang Yuzhi South China University of Technology
,
Guangzhou
,
China Correspondent:LIU Zhengyi professor
,
Dept.of Mechanical Engineering No.2
,
South China University of Technology
,
Guangzhou
,
China
金属学报(英文版)
The nature of“white layer”found in 55SiMnMo steel subjected to friction test has been stu- died using TEM,SEM,X-ray diffraction and EPMA techniques.It is shown that the struc- ture of the“white laver”on the rubbing surface is duplex,consisting of a special martensite and some austenite.This layer may be 25—50 μm thick.It is ultrafine,with grain diametric approximately 30 nm.Its micro-hardness may be as high as Hm 1500 and is capable of cut- ting glass.It has superb corrosion resistance and resists tempering.Its mierostructure and hardness undergo changes only when the steel is tempered above 500℃.
关键词:
friction
,
null
,
null
Jingpei XIE
,
Yaomin ZHU
,
Xiaoping WANG
材料科学技术（英文）
The M-s temperature, Delta G(gamma-->alpha), Delta G(gamma-->M) and mechanical energy under a non-severe impact loading in a medium manganese steel (Fe-7Mn-1.2C) have been calculated by means of Xu's Fe-X-C model. The relation between the yield strength of austenite and the driving force for martensite transformation has been established. It is proved that the martensite transformation can take place in a medium manganese steel (Fe-7Mn-1.2C alloy) under a non-severe impact loading.
关键词: