XU Changgan ZENG Zhongping Beijing University of Aeronautics and Astronautics
,
Beijing
,
China
金属学报(英文版)
The plots of load vs deflection(P-D)for two ultra-strength steels 30CrMnSiNi2A and 300M has been examined on a Charpy impact tester with digital memory and microcomputer. A criterion was found to availably represent the dynamic fracture toughness,K_(Ic)~D ,of the steels under impact loading.The K_(Ic)~D,.can be calculated with suggesting that the turning point of change in compliance on the P-D plot is the point of destabilized crack propagation.The K_(Ic)~D of steel 300M,quenched at 870℃ ,separately tempered at 300℃ and 450℃,was esti- mated to be 55—70 MN/m~(3/2)and 54—67 MN/m~(3/2)respectively.The K_(Ic)calculated with accuracy about 20% seems to be available to the engineering evaluation.
关键词:
ultra-strength steel
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,