RESEARCH A NEW TOOL STEEL AND ITS PROPERTIES FOR MAKING WOOD CHIP CUTTING KNIVES

X.N.Cheng , X.M.Luo and F.Jiang Department of Materials Engineering , Jiangsu University of Science and Technology , Nanjing 210013 , China

金属学报(英文版)

On the basis of analyses of service conditions and properties requirements of wood chip cutting knives, an alloying scheme was formulated and a kind of new tool steel was developed. Parameters for its heat treating process and mechanical properties were systematically investigated and optimized. Satisfactory results were obtained on the knives in practice.

关键词: wood chip cutting , null , null

Service Performance of Engineering Materials

Andrej Atrens

材料科学技术(英文)

Corrosion research by Atrens and co-workers has made significant contributions to the understanding of the service performance of engineering materials. This includes: (1) elucidated corrosion mechanisms of Mg alloys, stainless steels and Cu alloys, (2) developed an improved understanding of passivity in stainless steels and binary alloys such as Fe-Cr, Ni-Cr, Co-Cr, Fe-Ti, and Fe-Si, (3) developed an improved understanding of the melt spinning of Cu alloys, and (4) elucidated mechanisms of environment assisted fracture (EAF) of steels and Zr alloys. This paper summarises contributions in the following: (1) intergranular stress corrosion cracking of pipeline steels, (2) atmospheric corrosion and patination of Cu, (3) corrosion of Mg alloys, and (4) transgranular stress corrosion cracking of rock bolts.

关键词: Stress corrosion cracking , null , null

Biomimicry of bamboo bast fiber with engineering composite materials

Materials Science & Engineering C-Biomimetic Materials Sensors and Systems

Bamboo, one of the strongest natural structural composite materials, has many distinguishing features. It has been found that its reinforcement unit, hollow, multilayered and spirally-wound bast fiber, plays an extremely important role in its mechanical behavior. In the present work, on the basis of the study on bamboo bast fiber and wood tracheid, a biomimetic model of the reinforcing element, composed of two layers of helically wound fiber, was suggested. To detect the structural characteristics of such a microstructure, four types of macro fiber specimens made of engineering composites were employed: axially aligned solid and hollow cylinders, and single- and double-helical hollow cylinders. These specimens were subjected to several possible loadings, and the experimental results reveal that only the double-helical structural unit possesses the optimum comprehensive mechanical properties. An interlaminar transition zone model imitating bamboo bast fiber was proposed and was verified by engineering composite materials. In our work, the transition zone can increase the interlaminar shear strength of the composite materials by about 15%. These biomimetic structural models can be applied in the design and manufacture of engineering composite materials.

关键词: bamboo;bast fiber;biomimetics;engineering composites

Strengthening Materials by Engineering Coherent Internal Boundaries at the Nanoscale

Science

Strengthening materials traditionally involves the controlled creation of internal defects and boundaries so as to obstruct dislocation motion. Such strategies invariably compromise ductility, the ability of the material to deform, stretch, or change shape permanently without breaking. Here, we outline an approach to optimize strength and ductility by identifying three essential structural characteristics for boundaries: coherency with surrounding matrix, thermal and mechanical stability, and smallest feature size finer than 100 nanometers. We assess current understanding of strengthening and propose a methodology for engineering coherent, nanoscale internal boundaries, specifically those involving nanoscale twin boundaries. Additionally, we discuss perspectives on strengthening and preserving ductility, along with potential applications for improving failure tolerance, electrical conductivity, and resistance to electromigration.

关键词: strain-rate sensitivity;stacking-fault energy;nano-scale twins;cu-al;alloys;nanocrystalline metals;mechanical-properties;activation;volume;copper;deformation;behavior

STATISTICAL EVALUATION OF CRITICAL INCLUSION FACTOR FOR SECONDARY RECRYSTALLIZATON IN 3%Si STEEL Lecturer,Department of Materials Engineering,Southwestern Jiaotong University,Chengdu 610031,China

LI Shuchen Southwestern Jiaotong University , Chengdu , ChinaCHEN Mengzhe KE Jun University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

On the basis of statistical data of MnS in the conventional 3% Si steel sheeets after various annealing processes,the critical inclusion factor has been evaluated to be 20 mm~(-1).The inhi- bition of MnS to grain growth has been exactly described.

关键词: 3%Si steel , null , null

CORRELATION BETWEEN STRESS COMPONENTS AND STRESS CORROSION CRACKS IN BRASS Lecturer,Department of Materials Physics,University of Science and Technology Beijing,Beijing 100083,China

QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing , Beijing , China

金属学报(英文版)

The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.

关键词: stress corrosion cracking , null , null , null

Theoretical studies of g factors and defect structures for cubic, tetragonal, and orthorhombic Fe+ Centers in alkali halides MX (M = Li, Na; X = F, Cl)

Communications in Theoretical Physics

The EPR g factors for cubic, tetragonal and orthorhombic Fe+ centers in alkali halides MX (M = Li, Na; X = F, Cl) are calculated from second-order perturbation formulas of g factors based on cluster approach for 3d(7) ions in three symmetries. From calculations, the g factors of these Fe+ centers in MX crystals are reasonably explained and the defect structural data for the tetragonal and orthorhombic Fe+ centers are estimated. The results are discussed.

关键词: crystal;and ligand-field theory;electron paramagnetic resonance;defect structure;atomic screening constants;spin-orbit interaction;superposition model;resonance-spectra;epr parameters;crystal-field;scf functions;ions;co2+

Influence of plastic deformation upon the half-width of engineering metallic materials in hard state

Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science

The half-width values of the X-ray diffraction profiles are frequently used to characterize the static strength of a strengthened surface, or the depth distribution of this mechanical parameter, in a strengthened surface layer, especially in a shot-peening affected layer. However, for the unpeened surface and the base material of the shot-peened specimen of an alloy steel treated in hard state, the experimental results shown in this article indicate that uniaxial tensile or compressive plastic deformation increases the yield strengths while it decreases the half-width values. The half-width values of the shot-peened surface and surface layer greatly decrease, whereas the yield strength of this surface remarkably increases. Accordingly, in the authors' opinion, the half-width values could not correctly describe the static strengths of hard metallic materials, and, contrary to the viewpoint put forward by a lot of researchers, the shot-peened surfaces of such materials are work hardened instead of work softened. A model demonstrating that plastic deformation reduces the half-width values by decreasing the second kind internal stresses is developed.

关键词:

Effect of Heat Treatment Process on Mechanical Properties and Microstructure of Modified CNS-Ⅱ F/M Steel

YANG Ying , YAN Qing-zhi , MA Rong , GE Chang-chun

钢铁研究学报(英文版)

Ferritic/martensitic (F/M) steels have been recommended as one of the candidate materials for supercritical water cooled reactor (SCWR) in-core components use for its high thermal conductivity, low thermal expansion coefficient and inherently good dimensional stability under irradiation condition in comparison to austenitic steel. CNS-Ⅱ F/M steel which has good mechanical properties was one of the 9-12Cr F/M steels designed for SCWR in the previous work. In this study a modified CNS-Ⅱ F/M steel was used and it′s ultimate tensile strength was 925 MPa at room temperature and 483 MPa at 600 ℃ after optimizing heat treatment parameter. The ductile to brittle transition temperature of modified CNS-Ⅱ F/M steel is -55 ℃. Those are at the same level or even higher than that of CNS-Ⅱ and some commercial F/M steels nominated for SCWR in-core component use. The transmission electron microscope (TEM) results showed that the mechanical properties of the tempered martensite was closely related to the decomposition stage of the martensite.

关键词: supercritical water reactor , ferritic/martensitic steel , cladding material

  • 首页
  • 上一页
  • 1
  • 2
  • 3
  • 4
  • 5
  • 下一页
  • 末页
  • 共5217页
  • 跳转 Go

出版年份

刊物分类

相关作者

相关热词