Rheological Behavior of Semi-Solid AZ91D Alloy

Weimin MAO , Zisheng ZHEN , Shijian YAN , Xueyou ZHONG

材料科学技术(英文)

The rheological behavior and microstructure of semi-solid AZ91D was studied using a Couette type viscometer. The results show that the apparent viscosity of semi-solid AZ91D increases with the cooling rate increasing when it is continuously cooled and mechanically stirred and the empiric relation of the apparent viscosity with the cooling rate and solid fraction at shearing rate 93.7 s-1 is expressed as η=[0.66-0.63e(-ε3.01)]e (fs/0.14), and with the shearing rate and solid fraction at cooling rate 4ºC/min is shown as η=0.55e(fs/0.11- /87.59), as well as the cooling rate and shearing rate have an important effect on the microstructure of the semi-solid AZ91D alloy slurry, and decreasing the cooling rate and increasing the shearing rate are favorable to the nondendritic evolution of the primary grains.

关键词: Rheological behavior , null , null

Distribution of Microelements and Their Influence on the Corrosion Behavior of Aluminum Foil

Weimin MAO , Heng JIANG , Ping YANG , Huiping FENG , Yongning YU

材料科学技术(英文)

The distribution of microelement Fe, Si, Cu and Mg in the surface layer of aluminum foil annealed at 300℃ and 500℃ were determined by secondary ion mass spectrometer. The corrosion structure produced by electrochemical etching was also observed. It was found that the Mg concentration at external surface was increased exponentially over the fourth degree and promoted by higher annealing temperature, which will increase the number of corrosion pits inside the large grains, and therefore the specific capacity of the foils for electrolytic capacitors. The similar effects of microelement Fe, Si and Cu were not so strong.

关键词: Electrolytic capacitor , null , null , null

Texture Evaluation of α_2 Phase in Ti-25Al-10Nb-3V-1Mo Alloy Sheet

Weimin MAO , Yongning YU , Hong YANG and Bo SONG (Dept. of Materials Science and Engineering , University of Science and Technology Beijing , Beijing 100083 , China)

材料科学技术(英文)

The texture evaluation of α2 phase in Ti-25Al-10Nb-3V-1Mo sheet during rolling and annealing has been investigated by means of microstructure observation and ODF analysis. From the weak initial {1010} (1210) and {0001}(1210) textures a {1210}(1010) texture and a {0001}(uvtw)fibre texture are formed after cold rolling. The {0001} (1210) texture is also strengthened simultaneously. The activation process of slip systems is discussed concerning formation of the rolling texture. Because of the disappearance of {0001} (nvtw) fibre texture the primary recrystallization process should occur and the {1210}(1010) texture forms during annealing

关键词:

Preparation for Semi-Solid Aluminum Alloy Slurry under Weak Electromagnetic Stirring Conditions

Weimin MAO

材料科学技术(英文)

The effects of pouring temperature, short electromagnetic stirring with low strength and then soaking treatment on the microstructure of AlSi7Mg alloy were investigated. The results show that if AlSi7Mg alloy is poured at 630 or 650℃ and meanwhile stirred by an electromagnetic field at a low power for a short time, the pouring process can be easily controlled and most solidified primary α-Al grains become spherical and only a few of them are rosette-like. Weak electromagnetic stirring makes the temperature field more homogeneous and makes the primary α-Al grains disperse in a larger region, which leads to the spherical microstructures of primary α-Al grains. When the AlSi7Mg alloy is soaked or reheated at the semisolid state, the primary α-Al grains ripen further and they become more spherical, which is favorable to the semi-solid forming of AlSi7Mg alloy.

关键词: AlSi7Mg alloy , alloy , semi-solid , pouring , tempera

Formation of Copper Type Texture in Cold Rolled Aluminum Sheet

Weimin MAO

材料科学技术(英文)

The formation process of copper type rolling texture in f.c.c. metals was simulated based on a deformation model considering internal reaction stresses induced by the neighboring matrix as well as external shear stress induced by rollers. It is indicated that the external shear stress will reduce the brass type texture and increase the copper type texture obviously.

关键词: Texture , null , null , null

Slurry Preparation and Rolling of Semi-solid 60Si2Mn Spring Steel

Weimin MAO , Aimin ZHAO , Dong YUN , Leping ZHANG , Yonglin KANG

材料科学技术(英文)

The nondendritic semi-solid slurry preparation of 60Si2Mn spring steel has been studied in this paper. The experiments have shown that when stirred for 2 min on the test condition, the semi-solid slurry with 50%~60% fraction solid and spherical primary austenitic grains in the size of 100~300 μm can be obtained and is easy to be discharged from the bottom little hole of the stirring chamber. The nondendritic slurry of 60Si2Mn spring steel can be rolled into given plate form successfully, but the solid phase and liquid phase is easy to be separated in rolling process so that the solid primary austenite is concentrated in the center and the liquid is near the edge of the rolled plate. The rupture strength and elongation of the plate rolled only once with semi-solid slurry are lower than that of the traditionally repeated hot-rolled plate of 60Si2Mn spring steel.

关键词: 60Si2Mn , null , null , null

Influence of Surface Oxide Films on Elastic Behaviors of Straight Screw Dislocations Parallel to the Surface of Pure Aluminum

Weimin MAO , Dong LI

材料科学技术(英文)

The image stress of straight screw dislocations parallel to the medium surface covered by thin heterogeneous films was analyzed and deduced, in order to calculate the image shear stress. The relationship between image stress and distance from the screw dislocation to the interface of pure aluminum and its oxide covering was calculated based on the analysis. It was shown quantitatively that a sign conversion of the image stress appears in the case of thin oxide covering, while dislocation would pile up near the interface because of the possible slips of the screw dislocations induced by the image stress, which might break down the very thin oxide covering. Further investigation on edge dislocations or other dislocation configurations need to be done.

关键词: Dislocation , null , null , null , null , null , null

The preparation and corrosion behaviors of MAO coating on AZ91D with rare earth conversion precursor film

Applied Surface Science

A novel kind of micro-arc oxidation (MAO) coating was prepared on magnesium alloy surface coated with rare earth conversion film (RE-film) in an alkaline aluminum oxidation electrolyte by AC power source. Inspection of scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier transform infrared (FTIR) microspectroscopy, the structure and composition of MAO coating formed on AZ91D with RE-film under different applied voltages were investigated and the performance of the optimized MAO coating compared with the MAO coating directly formed on magnesium alloy. As the pretreatment of magnesium alloy with RE-film, the cerium oxides can be incorporated into the MAO coatings, reduce porosity of the MAO coating surface and enhance the thickness of MAO coating. These structure features and the cerium oxides incorporated into the MAO coating result in greatly improved corrosion resistance. Base on electrochemistry impedance spectroscopy (EIS) measurement, the electronic structure and composition analysis of the MAO coating, a double-layer structure, with a compact inner layer and a porous outer layer, of the coating was proposed for understanding its corrosion process. (C) 2010 Elsevier B.V. All rights reserved.

关键词: Magnesium alloy;Rare earth conversion film;Micro-arc oxidation;Porosity;az31 magnesium alloys;micro-arc oxidation;mg-al alloys;electrolyte;resistance;cerium;phosphate

Product/metal ratio (PMR): A novel criterion for the evaluation of electrolytes on micro-arc oxidation (MAO) of Mg and its alloys

Science China-Technological Sciences

Product/metal ratio (PMR) was introduced as a novel criterion for the evaluation of electrolytes on micro-arc oxidation (MAO) of Mg and its alloys. The criterion initially sprang from Pilling-Bedworth ratio (PBR), focused on the roles of electrolytes for the compactness of the fabricated coatings, and took attention on properties of reactants/products during MAO. Meanwhile, based on our experiments as well as the results from literatures, the effects of electrolyte additives on morphologies and compositions of the fabricated MAO coatings of Mg alloys were exploited for verification and supplement of the initial criterion. In combination of the initial PMR criterion and experimental verification, PMR could be represented by special mode (PMR (s)=V (oxide products)/V (alloy substrates)) and general mode (PMR (g)= PMR (s)+ PMR (d)). The ideal PMR (s) should be between 1 and 2, while PMR (d) is related to the coating deposition during MAO. PMR (d) is a supplement to PMR (s) when the effect of the overlaying property (O) of the coatings and the effective deposition (D) of electrolyte composites are considered (PMR (d)=f(O, D). O is related to the melting point (MP) and boiling point (BP) of the MAO products. D is related to the effective reactions between alloy substrates and electrolytes during MAO.

关键词: micro-arc oxidation;Mg alloys;Pilling-Bedworth ratio;product/metal;ratio;az91d magnesium alloy;electrochemical corrosion behavior;silicate-containing electrolytes;ceramic coatings;potassium fluoride;resistance;films;surface;microstructure;technology

Electrochemical corrosion behavior of composite coatings of sealed MAO film on magnesium alloy AZ91D

Electrochimica Acta

Protective composite coatings were prepared on magnesium alloy AZ91D by micro-arc oxidation (MAO) treatment plus a top coating with sealing agent using multi-immersion technique under low-pressure conditions. The corrosion resistance of AZ91D alloy with composite coatings was superior evidently to that with merely MAO film. SEM observations revealed that the sealing agent was integrated with MAO film by physically interlocking; therewith covered uniformly the surface as well as penetrated into pores and rnicro-cracks of MAO film. The anti-corrosion properties in 3.5% NaCl solution of the composite coatings were evaluated by using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements. Based on the results of chronopotentiometric (E similar to t) and EIS measurements for long time immersion in 3.5% NaCl solution, appropriate equivalent circuits for the composite coatings system were proposed. It follows that due to the blocking effect of the sealing agent in pores and cracks in MAO film, the composite coatings can suppress the corrosion process by holding back the transfer or diffusion of electrolyte and corrosion products between the composite coatings and solution during immersion. (c) 2005 Elsevier Ltd. All rights reserved.

关键词: composite coatings;MAO film;sealing;magnesium alloy AZ91D;EIS;micro-arc oxidation;impedance spectroscopy;interfacial factors;phosphate coatings;alkaline-solutions;aluminum-alloys;nacl solution;anodic films;mg alloys;part 2

  • 首页
  • 上一页
  • 1
  • 2
  • 3
  • 4
  • 5
  • 下一页
  • 末页
  • 共12页
  • 跳转 Go

出版年份

刊物分类

相关作者

相关热词