金属学报(英文版)
The effect of grain boundaries on cyclic deformation and fatigue crack growth in aluminum bicrystals has been studied.The effect of a grain boundary is restricted in a narrow area, termed as grain boundary affecting zone(GBAZ),where the incompatible plastic strain treats internal stress which conversely promotes inhomogeneous slip in the area and grain boundary cracking.As an extended stage I crack initiated from a notch approaches the grain boundary under a constant cyclic stress,the crack front branches splits into several pieces, meanwhile,the growth rate of the crack reduces to a minimum value at the center of the GBAZ.Such microstructure-sensitive growth of extended stage I cracks is mainly attributed to the grain boundary-induced crack tip sheilding.
关键词:
compatibility
,
null
,
null
,
null
X.F.Rong and Z.Y.Qin College of Mechanical Engineering
,
Taiyuan University of Technology
,
Taiyuan 030024
,
China
金属学报(英文版)
In this paper, a deposition feature of a SiC:H films deposited by a RF sputtering system and a effect on the hardness of the films with various deposition conditions are investigated, and the effects of the silicon on a C:H are studied. It follows from the results that the properties of hardness can be changed with the depositing conditions. An increase of silane in the gas phase allows to deposit a SiC:H having tetrahedral structure. The sets of deposition conditions by which the different types of a SiC:H films can be deposited are obtained.
关键词:
a SiC:H film
,
null
,
null
D.Eylon
,
S.R.Seagle
材料科学技术（英文）
The state of Ti research, development and industry is reviewed in this article. The fifty-year anniversary of Ti technology commercialization in the USA provides an opportunity for a historical perspective. Incorporation of "information-age" tools into alloy development, processing, and production invigorates the technology. Consolidation, diversification and globalization have been transforming the Ti industry in the recent years.
关键词:
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,
null
,
null
,
null
Yanwu Xu
材料科学技术（英文）
Using mathematical plasticity theories, universal formability (UF) technology has been developed and applied in the automotive stamping engineering and production. As a formability analysis tool, this technology is the major methodology for the development of stamping expert system (solution provider) for (a) product design and feasibility analysis, (b) material automatic selection using nomograms, (c) draw die design using pre-models, and (d) UF and robustness analysis of die performance in finite element analysis (FEA) environment.
关键词:
G.Montay
,
A.Cherouat
,
A.Nussair
,
J.Lu
材料科学技术（英文）
Residual stress in coatings is the result of individual particle stress. Their effects may be either beneficial or detrimental, depending upon the magnitude, sign and distribution of the stresses with respect to the external load. Tensile stress which exceeds the elastic limit causes cracking in surface coatings or at the interface between the substrate and the coat. Compressive stress, in general, has a beneficial effect on the fatigue life, crack propagation, coating adhesion and on the durability of the top coat during service. Compressive residual stresses can increase the number of cycles before crack initiation begins through a mean stress effect. Temperature gradients which occur during solidification and subsequent cooling are the principal mode of internal stresses generation. Some parameters influence the residual stress field of both the coating and the substrate. Substrate nature, spraying temperature, thickness of the coat layer, substrate preparation (grit blasting conditions), and velocity of the splats are in the relation with the quality of the coating. In this work, we will describe the role playing by the ceramics coating elaboration on the residual stress gradient in depth of the component. The incremental hole drilling technique has been developed to determine the residual stress gradient in depth of the coat and substrate which must be used with particularly conditions. This new technology has been employed on zirconia, alumina and tungsten carbide plasma sprayed coating.