Slag Melting Characteristic of Slag Forming and Slag Splashing for BOF Less Slag Smelting

WU Wei , MENG Hua-dong , LIU Liu , YUAN Tian-xiang , BAI Yan-jiang , YAN Zhan-hui

钢铁研究学报(英文版)

The slag melting characteristic of slag forming and slag splashing for 300 t BOF less slag process is researched by combining the methods of the slag chemical composition, the melting point determination and the petrographic analysis. The results show that the melting point of final slag for less slag smelting is 20 ℃ lower than that for conventional smelting. According to results of the petrographic analysis, the C3S (3CaO·SiO2) and C2S (2CaO·SiO2) content for less slag smelting are lower than those for conventional smelting, while the RO (FeO, MgO, MnO, etc) phase and C4AF (4CaO·Al2O3·Fe2O3) phase are higher than those for conventional smelting. According to results of the chemical analysis, the (CaO) content and slag basicity for less slag smelting are higher than those for conventional smelting, while (FeO) and (MgO) content in slag for less slag smelting are almost equal to those for conventional smelting. The reason why slag melting point for less slag smelting is lower than that for conventional smelting is that the quantity of added fluorite for less slag smelting is more than that for conventional smelting. According to the analysis results the slag melting point is determined by the C3S, C2S, RO phase and C4AF content. According to the results of slag melting characteristic before and after slag splashing for less slag smelting, the present adjusting slag process has little effect. It is important to adjust the composition of BOF final slag. The (FeO) content in slag is to be reduced at the slag splashing and adjusting slag process for less slag smelting.

关键词: less slag smelting , melting point determination , petrographic analysis , slag forming process , slag splashing

Ab initio study of the intrinsic exchange bias at the SrRuO(3)/SrMnO(3) interface

Physical Review B

In a recent publication [S. Dong et al., Phys. Rev. Lett. 103, 127201 (2009)], two (related) mechanisms were proposed to understand the intrinsic exchange bias present in oxides heterostructures involving G-type antiferromagnetic perovskites. The first mechanism is driven by the Dzyaloshinskii-Moriya interaction, which is a spin-orbit coupling effect. The second is induced by the ferroelectric polarization, and it is only active in heterostructures involving multiferroics. Using the SrRuO(3)/SrMnO(3) superlattice as a model system, density-functional calculations are here performed to verify the two proposals. This proof-of-principle calculation provides convincing evidence that qualitatively supports both proposals.

关键词: thin-films;weak ferromagnetism;superlattices;anisotropy;bifeo3;srruo3;model

NiO/FeCo磁性多层膜的高频磁性

李玉伟 , 陈继红 , 唐东明 , 张豹山 , 鹿牧 , 陆怀先

功能材料与器件学报 doi:10.3969/j.issn.1007-4252.2010.02.011

制备了一系列具有铁磁/反铁磁交换偏置作用的[NiO/Fe65Co35]10多层膜,使用振动样品磁强计(VSM)测量了样品的静磁参数,利用微带线法测量了样品4GHz-10GHz的磁谱,首次制备并测得了自然共振频率(fr)在6GHz以上,最高到f=9.6GHz的薄膜样品.结果表明交换偏置场(Hex)、各向异性场(Hua)、以及矫顽力(Hc)随铁磁层厚度(tFM)增大而减小;基于Landau-Lifishitz (L-L)方程对静磁参量和磁谱进行了比较,发现样品自然共振频率较L-L方程计算值偏大30%以上.

关键词: 铁磁 , 反铁磁 , 交换偏置场 , 各向异性场 , 交换耦合能密度 , 自然共振频率