材料科学技术（英文）
The recrystallization texture in commercially pure Al is investigated after the samples are rolled differently and annealed.The samples with low rol- ling reductions could be generally recovered or recrystallized in situ and characterized by the re- tained G{110}<001>component.This recovery process decreases during annealing with the increase of reduction.The appearance of the B/R{359}. <132>and R{123}<634>components de- pending on the rolling reduction is investigated and the less developed Cube{100}<001>component in commercially pure ahninium is also discussed.
关键词:
recrystallization
,
null
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词:
stress corrosion cracking
,