Energy-based models for predicting the low-cycle fatigue life of high-strength structural steels are presented. The models are based on energy dissipation during average of cycles, cycles to crack propagation and total cycles to failure. Plastic strain energy per cycle was determined and found as an important characteristic for initiation and propagation of fatigue cracks for high-strength structural steels. Fatigue strain-life curves were generated using plastic energy dissipation per cycle (loop area) and compared with the Coffin-Manson relation. Low cycle fatigue life was found similar from both methods. The material showed Masing-type behavior. The cyclic hysterisis energy per cycle was calculated from cyclic stress-strain parameters. The fracture surfaces of the fatigue samples were characterized by scanning electron microscope and the fracture mechanisms were discussed.
关键词:
low cycle fatigue
,
high-strength steel
,
energy-based model
,
fatigue life
章莎
,
周益春
材料导报
应用纳米压痕法测量残余应力的2种理论模型对5种电沉积镍镀层中的残余应力在不同压痕深度处进行了测量,并与X射线衍射法的测量结果进行了比较.结果表明,压深位于薄膜/基底界面处的2种压痕法测量结果与X射线衍射法的测量结果相近,且Yun-Hee模型与其符合得更好.
关键词:
纳米压痕法
,
电沉积镍镀层
,
残余应力
,
X射线衍射法
杨立新
,
巴黎明
,
李星
工程热物理学报
本文应用MUSIG模型[1]和均一直径模型对某溶液堆台架模型堆芯内气液流动传热进行了数值模拟.在MUSIG模型中堆芯内离散相气泡被分为5组不同直径的气泡,用于分析堆芯内气泡的流动变化和大小分布,采用Luo and Svendsen[2]和Prince and Blanch[3]模型描述不同直径气泡组间的破裂和聚合.在均一直径模型中,堆芯内的气体被考虑为同一直径的组分,并且不考虑其破裂与聚合现象.计算得到采用两个模型的模拟结果并且对其进行了对比研究.结果显示应用MUSIG模型的计算结果与台架实验结果吻合更好.
关键词:
MUSIG
,
均一直径
,
两相流
,
溶液堆