金属学报(英文版)
The size effect of tension round bars with circumferential crack was described and used to measure the plane-strain fracture toughness K_(1c) of median or low strength steel.The size of cylindrical specimen required for K_(1c) measurement is much smaller than that of standard specimen.The J-integral values of the cylindrical sqecimens were calculated to characterize the size effect.The finite element calculution and fracture morphology analysis have been conducted to eyplain the fact that smaller cylindrical specimen could be used to measure K_(1c) of median or low strength steel.
关键词:
median or low strength steel
,
null
,
null
QIAO Lijie LIU Rui XIAO Jimei University of Science and Technology Beijing
,
Beijing
,
China
金属学报(英文版)
The effects of stress components on nucleation sites and propagation directions of stress cor- rosion cracks in brass were investigated with specimens under mode Ⅱ and mode Ⅲ loadings. The results indicated that under mode Ⅱ loading,stress corrosion cracks nucleated on the site with maximum normal stress component and propagated along the plane perpendieular to the maximum normal stress,under mode Ⅲ loading,the stress corrosion crack was not evident on the 45°plane due to the general corrosion in aqueous solution with high NH_4OH concentra- tion,while stress corroded in aqueous solution with low NH_4OH concentration, numerous cracks with spacings of 10—150μm were found on the 45°plane with maximum normal stress and no stress corrosion cracks was observed on the plane with maximum shear stress.
关键词: