LIU Chaosan ZHANG Yongchang SHI Changxu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China professor
,
Institute of Metal Reserach
,
Academia Sinica
,
Shenyang
,
China
金属学报(英文版)
The melt spun ribbons of Al-La-Y-Ni(Fe)quaternary alloys were prepared by a single- roller melt spinning technique in vacuum.Their amorphous nature,mechanical properties and tensile fracture surface morphology were investigated.The experimental results show that amorphous alloys with high strength and good ductility as well as good thermal stability can be achieved in Al-La-Y-Ni(Fe)system,when the alloy contains 85—90 at.-% Al and less than 10 at.-% La+Y.The maximum tensile fracture strength(σ_f) and microhardness(HV)are as high as 760 MPa and 294 DPN,respectively.The as- quenched ribbons can be bent 180 degree without fracturing.The dominant factors for formation of amorphous Al-La-Y-Ni(Fe)are the strong attractive interaction among Al, La,Y and a decrease of melting temperature.
关键词:
single-roller melt spinning
,
null
,
null
,
null
MA Zongyi YAO Zhongkai Harbin Institute of Technology
,
Harbin
,
China
金属学报(英文版)
The SiC_w/Al composite prepared by squeeze casting has a combination of superior room temperature specific strength and modulus together with excellent thermal properties.The extrusion can make an improvement on the strength and ductility of the composite from 582 MPa as squeeze casted up to 639 MPa,and on the transformation from isotropic to the anisotropic structure.This seems to be explained by the orientation of whiskers and the densification of dislocations in matrix.TEM observation indicates that the stacking fault is the usual planar defect on the SiC_w surface. composite;;SiC whisker;;Al alloy;;microstructure
关键词:
composite
,
null
,
null
,
null
Corrosion
This paper introduces the design of a localized corrosion rate monitoring instrument that can monitor and evaluate the maximum and stable localized corrosion rate of a nonpassivable metal in a corrosive environment by measuring the current density in a corrosion sensor with an occluded anode.
关键词:
instrument;localized corrosion rate;monitor
Juhua HUANG
,
Jinjun RAO
,
Xuefeng LI
材料科学技术（英文）
Sheet metal forming is widely applied to automobile, aviation, space flight, ship, instrument, and appliance industries. In this paper, based on analyzing the shortcoming of general finite element analysis (FEA), the conception of parametric finite element analysis (PFEA) is presented. The parametric finite element analysis, artificial neural networks (ANN) and genetic algorithm (GA) are combined to research thoroughly on the problems of process parameters optimization of sheet metal forming. The author programs the optimization scheme and applies it in a research of optimization problem of inside square hole flanging technological parameters. The optimization result coincides well with the result of experiment. The research shows that the optimization scheme offers a good new way in die design and sheet metal forming field.
关键词:
Sheet metal forming
,
null
,
null
,
null
J.Q.ZHANGD.J.YOUNG
中国腐蚀与防护学报
Metaldusting attacks iron, low and high alloy steels and nickel-or cobalt-base alloys by disintegrating bulk metals and alloys into metal particles in a coke deposit. It occurs in strongly carburising gas atmospheres (carbon activity aC>1) at elevated temperatures (400 ℃~1000 ℃). This phenomenon has been studied for decades, but the detailed mechanism is still not well understood. Current methods of protection against metal dusting are either directed to the process conditions-temperature and gas composition-or to the development of a dense adherent oxide layer on the surface of the alloy by selective oxidation. However, metal dusting still occurs by carbon dissolving in the base metal via defects in the oxide scale. The research work at UNSW is aimed at determining the detailed mechanism of metal dusting of both ferritic and austenitic alloys, in particular the microprocesses of graphite deposition, nanoparticle formation and underlying metal destruction. This work was carried out using surface observation, cross-section analysis by focused ion beam and electron microscopic examination of coke deposits at different stages of the reaction. It was found that surface orientation affected carbon deposition and metal dusting at the initial stage of the reaction. Metal dusting occurred only when graphite grew into the metal interior where the volume expansion is responsible for metal disintegration and dusting. It was also found that the metal dusting process could be significantly changed by alterations in alloy chemistry. Germanium was found to affect the iron dusting process by destabilising Fe3C but increasing the rate of carbon deposition and dusting, which questions the role of cementite in ferritic alloy dusting. Whilst adding copper to iron did not change the carburisation kinetics, cementite formation and coke morphology, copper alloying reduced nickel and nickel-base alloy dusting rates significantly. Application of these fundamental results to the dusting behaviour of engineering alloys is discussed.
关键词:
metal dusting
,
null
,
null
,
null
,
null
,
null