To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of wCaO∶wCaF2=2∶1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290 ℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.
关键词:
LATS refining;ladle slag;melting point;additive;immersion cover
WANG Hongming
,
LI Guirong
,
LI Bo
,
et al
钢铁研究学报(英文版)
B2O3 is selected as fluxing agent of CaO-based ladle refining slag to decrease the melting temperature as well as to improve the speed of slag forming and the refining efficiency. The effects of B2O3 on the melting temperature of two series of refining slags including the low basicity slags (the mass ratio of CaO/SiO2 is 3~4) and the high basicity slags (the mass ratio of CaO/SiO2 is 5~8.75) were investigated. The slag melting temperature was measured using the hemisphere method. The results indicate that the fluxing action of B2O3 is better than that of CaF2 and Al2O3. For the CaO-based refining slag with low basicity, the melting temperature is decreased effectively when B2O3 is used to substitute for equal mass of CaF2, Al2O3 and SiO2, respectively. For the CaO-based refining slag with high basicity, when CaF2 is substituted with B2O3, the melting temperature can be decreased remarkably. Especially, when the mass ratios of CaO/Al2O3 and CaO/SiO2 are in range of 1.1~4.0 and 5.25~8.0, respectively, the slag melting temperature is lower than 1300℃. Therefore, the B2O3-containing refining slags with high ratios of CaO/Al2O3 and CaO/SiO2 have ultralow melting temperature. As a result, not only the slag forming speed but also the capabilities of desulfurizing, dephosphorizing and absorbing deoxidation products are expected to be improved.
关键词:
Fluoride-free slag;Boron oxide;CaO-based refining slag;Melting temperature;Basicity
孙丹丹
,
潘尚可
,
任国浩
,
吴云涛
,
商珊珊
,
张国庆
无机材料学报
doi:10.3724/SP.J.1077.2013.12735
针对Ce:Li6Lu(BO3)3晶体有效原子序数(zeff)高的问题,采用低原子序数的Y3+离子部分置换晶体中的Lu3+离子.通过固相合成法制备了Ce:Li6Lu1-xYx(BO3)3(0≤x≤1)固溶体.X射线粉末衍射(XRD)分析表明,该系列固溶体结构与Li6Gd(BO3)3晶体相同,空间群为P21/c.其X射线激发发射(XSL)的发光强度随着Y3+的含量增加而降低,当x=0.5时,固溶体的有效原子序数与Li6Gd(BO3)3闪烁体相当,但XSL发光强度是其1.4倍.Ce:Li6Lu0.5Y0.5(BO3)3的XSL光谱和PL光谱都在400 nm附近出现Ce3+离子的特征峰,可拟合出361和419 nm两个发光分量,分别对应于Ce3+离子的激发态电子的5d1→2F5/2和5d1→2F7/2能级跃迁.Ce:Li6Lu0.5Y0.5(BO3)3固溶体的衰减时间比Ce:Li6Lu(BO3)3略长,为19.6 ns.当x=0.50～0.70时,Ce:Li6Lu1-xYx(BO3)3(0≤x≤1)闪烁体比较适合作为中子探测材料.
关键词:
固相合成
,
Ce∶Li6LU1-xYx(BO3)3
,
X射线激发发射谱
,
PL光谱
,
衰减时间
陈俊锋
,
李赟
,
宋桂兰
,
姚冬敏
,
袁兰英
,
齐雪君
,
王绍华
无机材料学报
doi:10.3724/SP.J.1077.2006.01053
采用提拉法和铂坩埚感应加热技术生长出最大尺寸为直径25mm, 长40mm的Li6Gd(BO3)3:Ce晶体. XRD分析表明, 生长出的晶体为单一的Li6Gd(BO3)3:Ce相, 结构属P21/c空间群. 对晶体生长中存在的解理开裂、应力开裂及多晶问题进行了讨论, 并从晶体结构的角度解释了(020)完全解理面出现的原因. 晶体在380~800nm之间的透过率接近90%, 200~380nm之间的吸收是由Ce3+离子的4f-5d跃迁和Gd3+离子的4f-4f跃迁引起的. 不同激发源激发下的发射均显示Ce3+离子的双谱峰特征; 相比于紫外激发下的发射而言, X射线激发下的发射光谱略有红移. 该晶体发光符合单指数衰减模型, 衰减时间为30.74ns在241Am源的α射线激发下晶体的能量分辨率为28.84%.
关键词:
硼酸钆锂
,
crystal growth
,
optical transmittance
,
scintillation properties
陈俊锋
,
李赟
,
宋桂兰
,
姚冬敏
,
袁兰英
,
齐雪君
,
王绍华
无机材料学报
doi:10.3321/j.issn:1000-324X.2006.05.005
采用提拉法和铂坩埚感应加热技术生长出最大尺寸为直径25mm,长40mm的Li6Gd(BO3)3:Ce晶体.XRD分析表明,生长出的晶体为单一的Li6Gd(BO3)3:Ce相,结构属P21/c空间群.对晶体生长中存在的解理开裂、应力开裂及多晶问题进行了讨论,并从晶体结构的角度解释了(020)完全解理面出现的原因.晶体在380～800nm之间的透过率接近90%,200～380nm之间的吸收是由Ce3+离子的4f-5d跃迁和Gd3+离子的4f-4f跃迁引起的.不同激发源激发下的发射均显示Ce3+离子的双谱峰特征;相比于紫外激发下的发射而言,X射线激发下的发射光谱略有红移.该晶体发光符合单指数衰减模型,衰减时间为30.74ns,在241Am源的α射线激发下晶体的能量分辨率为28.84%.
关键词:
硼酸钆锂
,
晶体生长
,
光学透过
,
闪烁性能
唐骅
,
伍海浜
,
孟范成
硅酸盐通报
采用传统固相反应法制备了添加H3BO3助烧剂的Li2Zn3Ti4O12 (LZT)陶瓷,分别通过XRD、SEM、排水法及网络分析仪等方法研究了不同H3BO3添加量对所得陶瓷的物相、微观形貌、烧结特性与微波介电性能的影响.结果表明在LZT陶瓷中添加3wt% H3BO3可有效降低烧结温度,在900 ℃/2 h烧结条件下可以获得高致密性及优异的微波介电性:ρ=4.15 g/cm3,εr=17.916,Q×f=61200 GHz,Tf=-52.87×10-6/℃.
关键词:
微波介质陶瓷
,
Li2Zn3Ti4O12陶瓷
,
H3BO3
,
低温烧结
刘玮
,
潘尚可
,
李焕英
,
蒋勇
,
陈晓峰
,
任国浩
无机材料学报
doi:10.15541/jim20150080
为了提高中子探测效率,以富集10B的H310BO3为原料,通过提拉法生长了富集10B的Ce：Li6Lu(10BO3)3晶体。X射线激发发射光谱测试表明：其发光峰位于360~480 nm,属于Ce3+离子典型的5d -4f跃迁发光,其闪烁发光效率为BGO晶体的3.9倍。在350 nm紫外光和137Cs所发出的662 keV的γ射线激发下测得的衰减时间分别为21.0 ns和31.7 ns,在137Cs辐射源激发下所测得的相对光输出是CsI(Tl)晶体的20%,能量分辨率为9.7%。在慢化252Cf中子源激发下可以观测到明显的中子全能峰,其能量分辨率为33%。上述研究结果表明, Ce：Li6Lu(10BO3)3晶体具有较高的闪烁效率、快的衰减时间和良好的中子探测效率,是一种具有应用前景的中子探测用闪烁晶体。
关键词:
Ce:Li6Lu(10BO3)3晶体
,
中子探测
,
提拉法
,
闪烁晶体
陈俊锋
,
李赟
,
宋桂兰
,
姚冬敏
,
袁兰英
,
齐雪君
,
王绍华
无机材料学报
doi:10.3724/SP.J.1077.2007.00025
研究了80~500K范围内, 光激发下Li6Gd(BO3)3:Ce晶体发光和衰减的温度依赖特性. 在346nm光激发下, 热猝灭占优势, 发光随温度升高而降低. 在274nm光激发下, 发光由Gd3+向Ce3+的能量传递和热猝灭共同决定: 低于200K时, 能量传递占支配地位, 发光随温度升高而增强; 高于200K时, 热猝灭占优势, 发光随温度升高而减弱. 225K以下, 辐射跃迁占优势, 衰减随温度升高而略有增大; 225K以上, 无辐射跃迁占优势, 衰减随温度升高而减小. 利用经典的热猝灭公式和Arrhenius公式, 获取的激活能分别为0.33和0.32eV.
关键词:
发光
,
decay time
,
Li6Gd(BO3)3:Ce
,
temperature dependence
陈俊锋
,
李赟
,
宋桂兰
,
姚冬敏
,
袁兰英
,
齐雪君
,
王绍华
无机材料学报
doi:10.3321/j.issn:1000-324X.2007.01.005
研究了80～500 K范围内,光激发下Li6Gd(BO3)3∶Ce晶体发光和衰减的温度依赖特性.在346nm光激发下,热猝灭占优势,发光随温度升高而降低.在274nm光激发下,发光由Gd3+向Ce3+的能量传递和热猝灭共同决定:低于200K时,能量传递占支配地位,发光随温度升高而增强;高于200K时,热猝灭占优势,发光随温度升高而减弱.225K以下,辐射跃迁占优势,衰减随温度升高而略有增大;225K以上,无辐射跃迁占优势,衰减随温度升高而减小.利用经典的热猝灭公式和Arrhenius公式,获取的激活能分别为0.33和0.32eV.
关键词:
发光
,
衰减时间
,
Li6Gd(BO3)3∶Ce
,
温度依赖