Jian XU Xiukui SUN Wenxiu CHEN Wenduo WEI State Key Laboratory of RSA
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
材料科学技术（英文）
In present work.the ultrafine manganese particles were prepared by gas evaporation method.The structure,size distribution,growth morphology and surface oxidation for the particles were investi- gated by using X-ray diffraction and electron microscopy.The results indicated that three types of the particles,with the structure of α-Mn,β-Mn and one unknown,respectively existed in the man- ganese particles.The growth morphology of the particles depended on the size and intrinsic structure.When exposed to air,the particles were slightly oxidized only in the surface layer and sta- ble in air.
关键词:
ultrafine particle
,
null
,
null
,
null
Chunju WANG
,
Debin SHAN
,
Bin GUO
,
Jian ZHOU
,
Lining SUN
材料科学技术（英文）
From the viewpoint of production engineering, microforming is considered as an effective process to fabricate various microparts. Several key problems in microforming processes were investigated. A new microforming apparatus with a high stiffness piezoelectric actuator as the punch driver was developed to produce microparts. To improve the forming abilities and locate the billets, a floating microdie was designed. The size effects of the billets and die cavities on the microforming abilities were studied with upsetting and coining tests, respectively. And the isothermal microforming process of microgears was performed with the developed microforming apparatus. Several analysis methods were used to evaluate the forming quality of the microparts.
关键词:
Microforming
,
尺寸效应
,
微塑性成形设备
,
浮动
Express Polymer Letters
The state-of-art and key problems of carbon nanotube (CNT) based polymer composites (CNT/polymer composites) including CNT/polymer structural composites and CNT/polymer functional composites are reviewed. Based on the results reported up to now, CNTs can be an effective reinforcement for polymer matrices, and the tensile strength and elastic modulus of CNT/polymer composites can reach as high as 3600 MPa and 80 GPa, respectively. CNT/polymer composites are also promising functional composite materials with improved electrical and thermal conductivity, etc. Due to their multi-functional properties, CNT/polymer composites are expected to be used as low weight structural materials, optical devices, thermal interface materials, electric components, electromagnetic absorption materials, etc. However, the full potential of CNT/polymer composites still remains to be realized. A few key problems, such as how to prepare structure-controllable CNTs with high purity and consistently dependable high performance, how to break up entangled or bundled CNTs and then uniformly disperse and align them within a polymer matrix, how to improve the load transfer from matrix to CNT reinforcement, etc, still exist and need to be solved in order to realize the wide applications of these advanced composites.
关键词:
polymer composites;carbon nanotubes;mechanical properties;electrical;properties;thermal properties
李开明
,
李亚洲
,
冯维贵
,
林长
量子电子学报
doi:10.3969/j.issn.1007-5461.2007.05.014
采用非线性反馈控制,用附加了带参数的正弦项对Chen系统进行了有效的控制.随着参数k的逐渐增大,系统的动力学行为呈现出一系列的变化.数值研究结果表明:随控制参数的增大,驱动信号的强度渐大,混沌系统由混沌运动到周期轨道,最终到一相点.
关键词:
混沌
,
Chen系统
,
不动点
,
Lyapunov指数
,
反馈控制
Corrosion Science
The early stages of the evolution of atmospheric corrosion of carbon steels exposed in both a laboratory simulated and a natural atmosphere environment in Shenyang have been observed by in situ scanning electron microscopy. In the case of laboratory cyclic wet-dry tests, even though the chloride content level is very low, filiform corrosion is initiated in the early stage. The filiform corrosion grows in random directions, forming a network of ridges. White nodules nucleate and grow on the ridges during continued corrosion and eventually connect with each other to form the initial corrosion scale. Pits were also found on the surface beneath corrosion products. In the case of a natural atmospheric environment, both filiform corrosion and other localized corrosion, such as pitting and inter-granular attack take place in the initial stage. It is obvious that there is variety of localized corrosion in the initial stage of atmospheric corrosion. (C) 2007 Elsevier Ltd. All rights reserved.
关键词:
steel;atmospheric corrosion;initial stage;localized corrosion;in-situ;iron;electrolyte;thickness
材料科学技术（英文）
The key problems of cold power spinning of Ti-15-3 alloy are studied. Reasonable biller preparation methods are presented to improve crystal structure and avoid crack of billet. Influences of original wall thickness, reduction rate and feed rate on expanding in diameter are analyzed and some methods to prevent expanding in diameter are given.
关键词:
Debin SHAN
,
Yan LU
,
Ping LI
,
Yi XU
材料科学技术（英文）
The key problems of cold power spinning of Ti-15-3 alloy are studied. Reasonable biller preparation methods are presented to improve crystal structure and avoid crack of billet. Influences of original wall thickness, reduction rate and feed rate on expanding in diameter are analyzed and some methods to prevent expanding in diameter are given.
关键词:
Author S.T. TU
,
J.M. Gong and X. Ling Nanjing University of Chemical Technology
,
Nanjing 210009
,
ChinaManuscript received 18 October 1998
金属学报(英文版)
In order to interpret the test results of crossweld specimens for application in practical welded components, the present paper studies the high temperature behavior of laboratory cross weld specimens in terms of the uniaxial material tests and numerical simulations. It is found that the crossweld specimen may be used for the high temperature strength assessment, but can hardly be used for life assessment of the practical welded components, which depends on the loading conditions of the components.
关键词:
high temperature
,
null
,
null
,
null
,
null