机械工程材料
通过拉伸、冲击、弯曲、硬度和金相等试验对S355J2G3低合金钢MAG焊焊接接头的力学性能与显微组织进行了研究。结果表明：采用G383G3Sil焊丝对S355J2G3低合金钢进行焊接时，可获得拉伸、弯曲和冲击性能均良好的焊接接头；接头硬度的分布较均匀，最高不大于380HV；焊缝组织为沿柱状晶晶界析出的块状先共析铁素体，晶内为细小密集的针状铁素体和少量珠光体；热影响区组织主要为先共析铁素体、针状铁素体、珠光体和少量的粒状贝氏体；母材为均匀细小分布的铁素体和珠光体。
关键词:
S355J2G3低合金钢
,
焊接接头
,
力学性能
,
显微组织
Journal of Physics-Condensed Matter
The temperature dependences of the magnetization, internal energy and specific heat in a three-sublattice ferrimagnet or ferromagnet with /J(ab)/ = /J(bc)/ not equal /J(ca)/ are calculated within the framework of the linear spin-wave approximation, by employing retarded Green's functions. For both the ferromagnet and the ferrimagnet, the internal energy and the specific heat decrease with increasing J ' /J and/or the value of the spins. For fixed values of S,, Sb, S, and J ' /J, the internal energy and the specific heat increase, whereas the sublattice magnetization decreases with increasing temperature theta. The three-sublattice ferrimagnet has some particular characteristics which are not shown by the systems with two sublattices. For ferrimagnets, the antiferromagnetism of the system becomes weaker with increasing J ' /J. The sublattice magnetization at low temperatures (also the magnetization M(0) at 0 K) of a ferrimagnet increases with increasing J ' /J for fixed values of S(a), S(b) and S(c). The effects of the spins S(a) (S,) and Sb On the magnetizations of other sublattices differ. The characteristics of the a-sublattice are the same as those of the c-sublattice, due to their similarity as well as the symmetry of the system. The behaviours of the b-sublattice are different from those of the a- and c-sublattices, due to the asymmetry of the three-sublattice system. The spin-value dependences of the spin deviation Deltam per spin land also the energy for the zero-point quantum fluctuation) of the system are different for different sublattices. These differences are ascribed to the asymmetry of the three-sublattice systems, which leads to the new intrinsic properties of the systems.
关键词:
layered heisenberg ferrimagnets;spin-wave theory;elementary;excitations;superlattices;systems;magnetoresistance;antiferromagnet;interfaces
Doris Smith
,
Ken Lynam
环境化学
本文中使用安捷伦SPEC C18AR固相萃取膜盘成功萃取了水中的有机氯农药残留和除草剂.使用双柱配置的GC/μECD系统进行检测,安捷伦J&W DB-35ms UI超高惰性色谱柱作为分析柱,DB-XLB色谱柱为确认柱.该方法为浓度接近或低于最大污染限值的含氯有机物提供了高度灵敏的分析方法.根据预估的分析物萃取浓度,方法使用的校准范围为1-100 ng· mL-1.分别对0.01 μg·L-1的加标水样和一个自来水水样进行了萃取和分析,结果证明可满足水中的有机氯农药残留和除草剂的测定.
关键词:
有机氯农药
,
除草剂
,
色谱柱
Physical Review B
The Hamiltonian for a four-sublattice Heisenberg ferrimagnet or ferromagnet with different exchange constants (J(ab) = J(cd) not equal J(bc) = J(da)) was established. An extended Bogoliubov transformation was developed by solving an equation group, consisting of 20 equations and 20 unknowns. The procedure for solving the equation group was carried out by introducing a simple way of reducing the numbers of the equations and the unknowns. The spin-wave spectra in the present system have been determined by performing the standard Holstein-Primakoff transformation and the Bogoliubov one. It has been found that the spin-wave spectra of the present system depend on the exchange constants and that the degeneracy of the spin-wave spectra remains. The results for a special case (J(ab) = J(bc)) i.e., an antiferromagnet are discussed briefly. The spin-wave spectra of the four-sublattice Heisenberg antiferromagnet are found to be degenerative also and they are linear in k for small k.
关键词:
model
李振江
,
肖纳敏
,
李殿中
,
张俊勇
,
罗永建
,
张瑞雪
金属学报
doi:10.3724/SP.J.1037.2013.00747
以核电汽轮机缸体用G18CrMo2-6耐热钢为研究对象,分析了显微组织、第二相类型、形貌、尺寸和分布随回火温度的变化及其对冲击韧性的影响.结果表明,G18CrMo2-6钢正火经不同冷速冷却后得到不同的基体组织,经680℃回火后,冲击韧性均远高于指标要求,因此基体组织差异不是导致冲击韧性急剧恶化的决定性因素.经炉冷正火后在560～710℃区间回火,显微组织均为铁素体+回火贝氏体,随回火温度上升,室温冲击韧性增加.经560和600℃回火后,块状马氏体/奥氏体(M/A)岛、条状颗粒不均匀分布于贝氏体铁素体基体上,平均冲击韧性分别为17和29 J.710℃回火后块状M/A岛分解,条状颗粒转变为细小的颗粒状呈弥散分布,冲击韧性达到峰值93 J.除了基体组织的软化效应外,第二相的类型、形貌、尺寸和分布能够明显改变诱发裂纹萌生的临界断裂应力,是影响G 18CrMo2-6钢冲击性能的一个关键因素.
关键词:
G18CrMo2-6钢
,
回火温度
,
冲击韧性
,
碳化物
Journal of Materials Research
The morphology of the dark and bright regions observed by transmission electron microscopy for the Zr(64.13)Cu(15.75)Ni(10.12)Al(10) bulk metallic glass strongly depends on the ion beam parameters used for ion milling. This indicates that the ion beam could introduce surface fluctuation to metallic glasses during ion milling.
关键词:
room-temperature
Y.G. Cao
,
X.Y. Sun
金属学报(英文版)
J-integral and crack opening displacement δ(COD) were important parameters for characterization of fractures in engineering materials. The relationship between J-integral and COD has been investigated for a long time and was enerally represented as J = m σyδ, where σy is the yield strength and m is a function of specimen geometry and material properties. To determine the value of m, extensive studies and experiments have been performed. The method that used the fracture-surface topography analysis (FRASTA) for determining J-integral from fracture surfaces of materials was introduced. On the basis of the relationship between COD and fracture surface average profile, the relationship between J-integral and COD was deduced and compared with the generally used equation. The method was experimentally confirmed to be able to provide a new way to determine the relationship between J-integral and COD.