Effects of Microstructure of Aluminum Substrate on Ordered Nanopore Arrays in Anodic Alumina

Choong-Soo Chi , Jong-Ho Lee , Insoo Kim , Han-Jun Oh

材料科学技术（英文）

关键词:

Effect of Palladium Nanoparticles on Photocatalytic Characteristics of N doped Titania Catalyst

Jong-Ho Lee , Jeong-Il Youn , Young-Jig Kim , Han-Jun Oh

材料科学技术（英文）

关键词:

HAN液晶盒中开关时间对形变场弛豫过程的影响

李晓吉 , 郑桂丽 , 张志东

液晶与显示 doi:10.3788/YJYXS20132801.0025

在HAN液晶盒撤掉外加电压的过程(即弛豫过程)中,假定电压的开关时间为有限的,把电压处理为时间的指数衰减函数.在这一假定下,对撤掉外加电压后HAN液晶盒中指向矢的分布情况进行研究,得到了对HAN液晶盒的弛豫过程有影响的电压开关时间的范围.

关键词: HAN液晶盒 , 有限开关时间 , 驰豫过程 , 动力学理论

电场诱导纳米结构HAN液晶盒中新型有序重构过程的描述

陈思博 , 王永超 , 周璇 , 张志东

液晶与显示 doi:10.3788/YJYXS20163109.0853

基于 Landau-de Gennes 理论，利用松弛迭代的方法，研究了包含－1/2向错线的混合排列(HAN)液晶盒中，平行于向错线的电场所诱导的结构转变。结果表明，盒厚固定时，电场诱导五种结构转变过程；电场固定时，盒厚变化产生三类结构转变方式。力曲线上的极小值确定了液晶系统发生结构转变的临界盒厚。

关键词: 有序重构 , Landau-de Gennes理论 , -1/2 向错 , 力曲线

复合包覆Co(OH)x+Yb(OH)3的Ni(OH)2正极材料的高温性能研究

赫文秀 , 安胜利 , 张永强 , 孙海峰 , 杨慧 , 蒋文全

中国稀土学报

化学共沉淀法合成氢氧化镍,并在表面用"梯度共晶法"复合包覆Co(OH)x+Yb(OH)3.XRD,XPS,SEM表征结果表明:制备的样品为六方球形β-Ni(OH)2,表面包覆了Co(OH)x+Yb(OH)3,Co的存在形式应该主要为Co2+及少量的Co3+.65℃下0.2C,1C和3c恒电流充放电时,复合包覆Co(OH)x+2%Yb(OH)3的氢氧化镍的放电比容量和放电效率最大.大倍率充放电和循环稳定性等性能也得到改善.

关键词: 包覆 , 放电容量 , 循环性能 , Yb(OH)3 , 稀土

Thermodynamic Analysis of Thermal Decomposition of Al(OH)_3

Wenming ZENG and Nianyi CHEN(Shanghai Institute of Metallurgy Chinese Academy of Sciences , Shanghai 200050 , China)

材料科学技术（英文）

Thermodynamic analysis of the main reactions in the process of thermal decomposition ofAl(OH)3 was made using Temkin-Schwarzman's method and by means of regression analysis.

关键词:

Kinetics of α-FeO(OH)Formation in Weak Acidic Medium

By ZHANG Yi WANG Yingxia HUA Tongwen Institute of Chemical Metallurgy , Academia Sinica , Beijing , 100080 , China.Department of Chemistry , Peking University , Beijing , 100871 , China.To whom correspondence should be addressed.

材料科学技术（英文）

The kinetics of α-FeO(OH) formation in weak acidic medium was studied.The effects of the initial concentration,temperature,pH value,partial pres- sure of oxygen,air flow rate and agitating intensity on the oxidation rate of Fe(OH)_2 suspensions have been investigated.It is confirmed that the reaction order for Fe(Ⅱ) is zero at the stage of α-FeO(OH) seeds formation,and about 0.5 at the stage of the seeds growth,and in the whole process partial pres- sure of oxygen appears in first order.The activation energy is determined.The dissolution-oxidation equilibrium which exists in the process of seeds formation has been suggested,by which the zero order reaction for Fe(Ⅱ) and the plateau in the pH-t curve were explained.Physical process is the rate-determining step of the heterogeneous reaction.The study on the kinetics of α-FeO(OH) formation may provide some fundamental informa- tion for the reactor design,the engineering amplifi- cation and the optimization control in the industrial process.

关键词: kinetics , null , null , null

掺钇α-Ni(OH)2的研究

杨书廷 , 陈改荣 , 尹艳红 , 陈红军 , 贾俊华

应用化学 doi:10.3969/j.issn.1000-0518.2001.09.003

采用均匀络合共沉淀法,首次合成出了掺杂钇基a-Ni(OH)2.并采用XRD,FTIR和SEM分析技术,对其结构及形貌进行了研究.电化学测试表明,所制得的掺杂钇基a-Ni(OH)2与掺铝的α-Ni(OH)2和球形β-Ni(OH)2相比,敲实密度1.6 g/cm2,电化学比容量330 mA@h/g以上,活性物质利用率大于95%,循环可逆性好等优点.

关键词: a-Ni(OH)2,钇,掺杂,电化学性能

Mg(OH)2晶须的制备

吴健松 , 肖应凯 , 张丽 , 匡文华 , 梁海群 , 吴康娣

应用化学 doi:10.3969/j.issn.1000-0518.2008.05.006

以MgCl2为原料,NaOH为沉淀剂,研究了它们的浓度配比、反应温度、晶化温度、晶化时间、晶化方式等因素对形成Mg(OH)2晶须的影响. 结果表明,当n(MgCl2): n(NaOH)=1.20: 1.92、混合温度Tm=86 ℃、晶化温度Tc=100 ℃、晶化时间Time=5.5 h时,可以得到发育不完全的初级Mg(OH)2晶须. 若改用水热法晶化,可得到发育较好的Mg(OH)2晶须. 在此基础上,若在NaOH溶液中加入一定量的有机溶剂OR(NaOH浓度不变)时,即可得到发育更完善的Mg(OH)2晶须. 电子显微镜照片显示,粒子呈晶须形状,粒度分布均匀,分散性好,晶形好,纯度高. 并对晶须生长机理进行了初步分析.

关键词: Mg(OH)2 , 晶须 , 水热法 , 功能材料

Al(OH)3和Sr(OH)2复合粉末的制备及性能研究

胡劲 , 孙家林 , 刘建良 , 施安 , 徐茂 , 高勤琴

人工晶体学报 doi:10.3969/j.issn.1000-985X.2006.01.016

本文采用活化Al-Sr合金粉末水解反应制备Al(OH)3和Sr(OH)2复合粉末,利用XRD,SEM,EDS,BET及激光粒度仪对复合粉末进行结构和性能研究.研究结果表明,Al(OH)3和Sr(OH)2的复合粉末中Sr/Al比例与配比相比有所偏移,但在复合粉末中两者均匀混合,具有化学组成的微观均匀性.复合粉末微观形貌为1～3μm片状小颗粒叠加的团聚颗粒,BET比表面积较大,达到45.2m2/g,水解产物粒度分布均匀,D50为27.58μm,D25/D75为0.76.

关键词: Al-Sr合金 , 水解 , 复合粉末